Electrical properties of flash-evaporated carbon nanolayers on PTFE

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22310%2F10%3A00022993" target="_blank" >RIV/60461373:22310/10:00022993 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Electrical properties of flash-evaporated carbon nanolayers on PTFE

Popis výsledku v původním jazyce

Carbon nano-layers were prepared by carbon flash evaporation on polytetrafluoroethylene. The electrical resistance of the carbon layers deposited onto PTFE by flash evaporation was measured as a function of the sample temperature. Monotonous decrease ofthe layer resistance with increasing temperature indicates semiconducting character of the carbon layers. The charge transport in the temperature range from 80-350 K is well described by Mott?s variable range hopping mechanism. The layers exhibit non-linear dependence of the electrical current on the applied voltage which indicates departure from ohmic mechanism of the charge transport. The optical gap width was determined to be Egopt = 0.1 eV from UV-Vis spectra.

Název v anglickém jazyce

Electrical properties of flash-evaporated carbon nanolayers on PTFE

Popis výsledku anglicky

Carbon nano-layers were prepared by carbon flash evaporation on polytetrafluoroethylene. The electrical resistance of the carbon layers deposited onto PTFE by flash evaporation was measured as a function of the sample temperature. Monotonous decrease ofthe layer resistance with increasing temperature indicates semiconducting character of the carbon layers. The charge transport in the temperature range from 80-350 K is well described by Mott?s variable range hopping mechanism. The layers exhibit non-linear dependence of the electrical current on the applied voltage which indicates departure from ohmic mechanism of the charge transport. The optical gap width was determined to be Egopt = 0.1 eV from UV-Vis spectra.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CD - Makromolekulární chemie

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Materials Science

ISSN

0022-2461

e-ISSN

—

Svazek periodika

45

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

DE - Spolková republika Německo

Počet stran výsledku

3

Strana od-do

—

Kód UT WoS článku

000272904700037

EID výsledku v databázi Scopus

—