Annealing of sputtered gold nano-structures
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22310%2F11%3A43892540" target="_blank" >RIV/60461373:22310/11:43892540 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/44555601:13440/11:43878466
Výsledek na webu
<a href="http://dx.doi.org/10.1007/s00339-010-5977-5" target="_blank" >http://dx.doi.org/10.1007/s00339-010-5977-5</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1007/s00339-010-5977-5" target="_blank" >10.1007/s00339-010-5977-5</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Annealing of sputtered gold nano-structures
Popis výsledku v původním jazyce
The effects of annealing on gold structures sputtered onto glass substrate were studied using AFM, UV-Vis methods and electrical measurements. The colour of the as-deposited films changes from blue to green with increasing deposition time. After 1 hour annealing at 300 degrees C the structures acquire red colour regardless of the film thickness. The annealing results in dramatic changes of surface morphology and roughness and creation of relatively large "spherolytic and hummock-like" structures in thegold layer. For deposited structures a non-zero optical band gap E(g)(opt) was determined from UV-Vis spectra using Tauc's model and it indicates a semi-conducting character of the structures. The annealing leads to an increase of the band gap. Electrical resistance of the deposited unannealed structures decreases dramatically for deposition times above 50 s. For annealed structures the resistance fall comes until after 250 s deposition time.
Název v anglickém jazyce
Annealing of sputtered gold nano-structures
Popis výsledku anglicky
The effects of annealing on gold structures sputtered onto glass substrate were studied using AFM, UV-Vis methods and electrical measurements. The colour of the as-deposited films changes from blue to green with increasing deposition time. After 1 hour annealing at 300 degrees C the structures acquire red colour regardless of the film thickness. The annealing results in dramatic changes of surface morphology and roughness and creation of relatively large "spherolytic and hummock-like" structures in thegold layer. For deposited structures a non-zero optical band gap E(g)(opt) was determined from UV-Vis spectra using Tauc's model and it indicates a semi-conducting character of the structures. The annealing leads to an increase of the band gap. Electrical resistance of the deposited unannealed structures decreases dramatically for deposition times above 50 s. For annealed structures the resistance fall comes until after 250 s deposition time.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CD - Makromolekulární chemie
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2011
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Applied Physics A-Materials Science & Processing
ISSN
0947-8396
e-ISSN
—
Svazek periodika
102
Číslo periodika v rámci svazku
3
Stát vydavatele periodika
US - Spojené státy americké
Počet stran výsledku
5
Strana od-do
747-751
Kód UT WoS článku
000287320600035
EID výsledku v databázi Scopus
—