Effect of acid pickling on mechanical properties of high-strength steel
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22310%2F12%3A43894728" target="_blank" >RIV/60461373:22310/12:43894728 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Effect of acid pickling on mechanical properties of high-strength steel
Popis výsledku v původním jazyce
Hydrogen forming during acid pickling can enter steel structure and change its mechanical properties. Both the bulk and the surface changes can have severe consequences, especially for steels used in power plant or aerial industry. The aim of this work was to describe the effect of acid pickling on mechanical properties of high strength steels. We used samples of 15-5PH - martensitic, precipitation-strengthened steel. We tested effect of different acid solutions (HCl/HCl + inhibitors) and varying conditions of pickling (cathodic polarization, skipping the annealing for hydrogen removal) on hydrogen diffusion coefficient, tensile and three-point bend transverse strength. The structure of fracture area was evaluated using scanning electron microscopy. The hydrogen diffusion coefficient value suggested that the hydrogen penetration was very shallow. The fractographical evaluation of the fracture area revealed presence of brittle fracture only in the surface area of the specimen. Ultimatel
Název v anglickém jazyce
Effect of acid pickling on mechanical properties of high-strength steel
Popis výsledku anglicky
Hydrogen forming during acid pickling can enter steel structure and change its mechanical properties. Both the bulk and the surface changes can have severe consequences, especially for steels used in power plant or aerial industry. The aim of this work was to describe the effect of acid pickling on mechanical properties of high strength steels. We used samples of 15-5PH - martensitic, precipitation-strengthened steel. We tested effect of different acid solutions (HCl/HCl + inhibitors) and varying conditions of pickling (cathodic polarization, skipping the annealing for hydrogen removal) on hydrogen diffusion coefficient, tensile and three-point bend transverse strength. The structure of fracture area was evaluated using scanning electron microscopy. The hydrogen diffusion coefficient value suggested that the hydrogen penetration was very shallow. The fractographical evaluation of the fracture area revealed presence of brittle fracture only in the surface area of the specimen. Ultimatel
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JK - Koroze a povrchové úpravy materiálu
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/FR-TI1%2F086" target="_blank" >FR-TI1/086: Nové přístupy navrhování energetických zařízení a ocelových konstrukcí s vysokými užitnými parametry</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2012
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Proceedings of 19th International Students' Day of Metallurgy
ISBN
978-3-00-037493-7
ISSN
—
e-ISSN
—
Počet stran výsledku
6
Strana od-do
214-220
Název nakladatele
Dzierzon Druck
Místo vydání
Freiberg
Místo konání akce
Freiberg
Datum konání akce
15. 3. 2012
Typ akce podle státní příslušnosti
EUR - Evropská akce
Kód UT WoS článku
—