Structural characteristics and corrosion behavior of biodegradable Mg-Zn, Mg-Zn-Gd alloys

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22310%2F13%3A43896489" target="_blank" >RIV/60461373:22310/13:43896489 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/60461373:22340/13:43896489

Výsledek na webu

<a href="http://dx.doi.org/10.1007/s10856-013-4916-3" target="_blank" >http://dx.doi.org/10.1007/s10856-013-4916-3</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1007/s10856-013-4916-3" target="_blank" >10.1007/s10856-013-4916-3</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Structural characteristics and corrosion behavior of biodegradable Mg-Zn, Mg-Zn-Gd alloys

Popis výsledku v původním jazyce

In this research, binary Mg-Zn (up to 3 wt% Zn) and ternary Mg-Zn-Gd (up to 3 wt% Gd, 3 wt% Zn) alloys were prepared by induction melting in an argon atmosphere. The structures of these alloys were characterized using light and scanning electron microscopy, energy dispersive spectrometry, X-ray diffraction and X-ray fluorescence. In addition, Brinell hardness measurements were taken to supplement these studies. Corrosion behavior was evaluated by immersion tests and potentiodynamic measurements in a physiological solution (9 g/l NaCl). Depending on the composition, structures of the as-cast alloys contained alpha-Mg dendrites, MgZn, Mg5Gd and Mg3Gd2Zn3 phases. Compared to pure Mg, zinc improved the corrosion resistance of binary Mg-Zn. Gadolinium alsoimproved the corrosion resistance in the case of Mg-1Zn-3Gd alloy. The highest corrosion rate was observed for Mg-3Zn-3Gd alloy. Our results improve the understanding of the relationships between the structure and corrosion behavior of ou

Název v anglickém jazyce

Structural characteristics and corrosion behavior of biodegradable Mg-Zn, Mg-Zn-Gd alloys

Popis výsledku anglicky

In this research, binary Mg-Zn (up to 3 wt% Zn) and ternary Mg-Zn-Gd (up to 3 wt% Gd, 3 wt% Zn) alloys were prepared by induction melting in an argon atmosphere. The structures of these alloys were characterized using light and scanning electron microscopy, energy dispersive spectrometry, X-ray diffraction and X-ray fluorescence. In addition, Brinell hardness measurements were taken to supplement these studies. Corrosion behavior was evaluated by immersion tests and potentiodynamic measurements in a physiological solution (9 g/l NaCl). Depending on the composition, structures of the as-cast alloys contained alpha-Mg dendrites, MgZn, Mg5Gd and Mg3Gd2Zn3 phases. Compared to pure Mg, zinc improved the corrosion resistance of binary Mg-Zn. Gadolinium alsoimproved the corrosion resistance in the case of Mg-1Zn-3Gd alloy. The highest corrosion rate was observed for Mg-3Zn-3Gd alloy. Our results improve the understanding of the relationships between the structure and corrosion behavior of ou

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GBP108%2F12%2FG043" target="_blank" >GBP108/12/G043: Mikro- a nanokrystalické materiály s vysokým podílem rozhraní pro moderní strukturní aplikace, biodegradabilní implantáty a uchovávání vodíku</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2013

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Materials Science: Materials in Medical

ISSN

0957-4530

e-ISSN

—

Svazek periodika

24

Číslo periodika v rámci svazku

7

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

12

Strana od-do

1615-1626

Kód UT WoS článku

000320962100001

EID výsledku v databázi Scopus

—