Mechanical Properties and Thermal Stability of Al-Si-X Based Alloys
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22310%2F13%3A43896537" target="_blank" >RIV/60461373:22310/13:43896537 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Mechanical Properties and Thermal Stability of Al-Si-X Based Alloys
Popis výsledku v původním jazyce
Aluminium based alloys are well known for their low density and convenient mechanical properties filling the imaginary gap between titanium alloys and common aluminium alloys. Aluminium alloys prepared via centrifugal atomization technique (CA) can contain higher amount of transition metals (Fe, Cr, Mn), characterized by low diffusivity in solid aluminium, enhancing their properties, especially thermal stability. In this work, AlSi23Fe8Cr1 and AlSi23Fe8Mn5 (in wt. %) alloys were prepared via centrifugalatomization. Prepared powders were compactized by uni-axial pressing at 6 GPa and 450 °C for 60 min. The microstructure of prepared powders and compact samples was studied by light (LM) and electron scanning microscopy (SEM). Phase composition was determined by X-ray diffraction (XRD). The thermal stability of the alloys was studied by mechanical testing after long-term annealing at 300-400 °C and by creep testing at 300 °C and compressive stress of 250 MPa. Obtained results were compar
Název v anglickém jazyce
Mechanical Properties and Thermal Stability of Al-Si-X Based Alloys
Popis výsledku anglicky
Aluminium based alloys are well known for their low density and convenient mechanical properties filling the imaginary gap between titanium alloys and common aluminium alloys. Aluminium alloys prepared via centrifugal atomization technique (CA) can contain higher amount of transition metals (Fe, Cr, Mn), characterized by low diffusivity in solid aluminium, enhancing their properties, especially thermal stability. In this work, AlSi23Fe8Cr1 and AlSi23Fe8Mn5 (in wt. %) alloys were prepared via centrifugalatomization. Prepared powders were compactized by uni-axial pressing at 6 GPa and 450 °C for 60 min. The microstructure of prepared powders and compact samples was studied by light (LM) and electron scanning microscopy (SEM). Phase composition was determined by X-ray diffraction (XRD). The thermal stability of the alloys was studied by mechanical testing after long-term annealing at 300-400 °C and by creep testing at 300 °C and compressive stress of 250 MPa. Obtained results were compar
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GBP108%2F12%2FG043" target="_blank" >GBP108/12/G043: Mikro- a nanokrystalické materiály s vysokým podílem rozhraní pro moderní strukturní aplikace, biodegradabilní implantáty a uchovávání vodíku</a><br>
Návaznosti
S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2013
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Conference METAL 2013 proceedings
ISBN
978-80-87294-39-0
ISSN
—
e-ISSN
—
Počet stran výsledku
7
Strana od-do
1189-1195
Název nakladatele
Tanger, spol. s r.o.
Místo vydání
Ostrava
Místo konání akce
Brno
Datum konání akce
15. 5. 2013
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—