Preparation and properties of boride layers on TiAl

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22310%2F13%3A43896545" target="_blank" >RIV/60461373:22310/13:43896545 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Preparation and properties of boride layers on TiAl

Popis výsledku v původním jazyce

Ti-46.6Al, Ti-45.2Al-7.2Nb and Ti-44.8Al-6.6Ta alloys were borided by a simple pack-boriding method in this work. After boriding at 1150 °C for 12 hours the layer deposited on the binary alloy exhibited a homogeneous both structure and chemical composition. The layers on the ternary alloys were thicker than those on the binary alloy with significantly higher structural and chemical heterogeneity. The mixed borides TiB2.NbB2 or TiB2.TaB2 were formed on the surfaces of these alloys, and monoboride whiskers were found at the boride/substrate interface. The surface hardness and the wear resistances of the examined alloys were significantly improved through their boriding.

Název v anglickém jazyce

Preparation and properties of boride layers on TiAl

Popis výsledku anglicky

Ti-46.6Al, Ti-45.2Al-7.2Nb and Ti-44.8Al-6.6Ta alloys were borided by a simple pack-boriding method in this work. After boriding at 1150 °C for 12 hours the layer deposited on the binary alloy exhibited a homogeneous both structure and chemical composition. The layers on the ternary alloys were thicker than those on the binary alloy with significantly higher structural and chemical heterogeneity. The mixed borides TiB2.NbB2 or TiB2.TaB2 were formed on the surfaces of these alloys, and monoboride whiskers were found at the boride/substrate interface. The surface hardness and the wear resistances of the examined alloys were significantly improved through their boriding.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GBP108%2F12%2FG043" target="_blank" >GBP108/12/G043: Mikro- a nanokrystalické materiály s vysokým podílem rozhraní pro moderní strukturní aplikace, biodegradabilní implantáty a uchovávání vodíku</a><br>

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2013

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Conference METAL 2013 proceedings

ISBN

978-80-87294-39-0

ISSN

—

e-ISSN

—

Počet stran výsledku

7

Strana od-do

1347-1353

Název nakladatele

Tanger, spol. s r.o.

Místo vydání

Ostrava

Místo konání akce

Brno

Datum konání akce

15. 5. 2013

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—