Powder metallurgy preparation of porous titanium for medical implants
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22310%2F13%3A43896671" target="_blank" >RIV/60461373:22310/13:43896671 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Powder metallurgy preparation of porous titanium for medical implants
Popis výsledku v původním jazyce
Porous biomaterials are used for implants to improve the osseointegration and to achieve the mechanical properties closer to the human bone. In this work, conditions of the powder metallurgy process were optimized to obtain porous biomaterial. The effects of titanium particle size, pressure used for powder pressing and sintering temperature on the porosity and mechanical properties were determined. The most significant effect on the porosity was found in the case of the size of titanium particles. The addition of the pore-forming agent was also successfully tested. As the pore former, the water-soluble salt (NaCl) was applied. A mixture of titanium and salt was prepared, compressed and leached in distilled water. After that, sintering was carried out under the optimized conditions.
Název v anglickém jazyce
Powder metallurgy preparation of porous titanium for medical implants
Popis výsledku anglicky
Porous biomaterials are used for implants to improve the osseointegration and to achieve the mechanical properties closer to the human bone. In this work, conditions of the powder metallurgy process were optimized to obtain porous biomaterial. The effects of titanium particle size, pressure used for powder pressing and sintering temperature on the porosity and mechanical properties were determined. The most significant effect on the porosity was found in the case of the size of titanium particles. The addition of the pore-forming agent was also successfully tested. As the pore former, the water-soluble salt (NaCl) was applied. A mixture of titanium and salt was prepared, compressed and leached in distilled water. After that, sintering was carried out under the optimized conditions.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/TE01020390" target="_blank" >TE01020390: Centrum vývoje moderních kovových biomateriálů pro lékařské implantáty</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2013
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Conference METAL 2013 proceedings
ISBN
978-80-87294-39-0
ISSN
—
e-ISSN
—
Počet stran výsledku
6
Strana od-do
1301-1306
Název nakladatele
Tanger, spol. s r.o.
Místo vydání
Ostrava
Místo konání akce
Brno
Datum konání akce
15. 5. 2013
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—