Preparation of periodic surface structures on doped poly(methyl metacrylate) films by irradiation with KrF excimer laser
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22310%2F14%3A43897953" target="_blank" >RIV/60461373:22310/14:43897953 - isvavai.cz</a>
Výsledek na webu
<a href="http://www.nanoscalereslett.com/content/9/1/591" target="_blank" >http://www.nanoscalereslett.com/content/9/1/591</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1186/1556-276X-9-591" target="_blank" >10.1186/1556-276X-9-591</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Preparation of periodic surface structures on doped poly(methyl metacrylate) films by irradiation with KrF excimer laser
Popis výsledku v původním jazyce
In this work, we describe laser modification of poly(methyl methacrylate) films doped with Fast Red ITR, followed by dopant exclusion from the bulk polymer. By this procedure, the polymer can be modified under extremely mild conditions. Creation of surface ordered structure was observed already after application of 15 pulses and 12 mJ cm(-2) fluence. Formation of grating begins in the hottest places and tends to form concentric semi-circles around them. The mechanism of surface ordered structure formation is attributed to polymer ablation, which is more pronounced in the place of higher light intensity. The smoothness of the underlying substrate plays a key role in the quality of surface ordered structure. Most regular grating structures were obtainedon polymer films deposited on atomically 'flat' Si substrates. After laser patterning, the dopant was removed from the polymer by soaking the film in methanol.
Název v anglickém jazyce
Preparation of periodic surface structures on doped poly(methyl metacrylate) films by irradiation with KrF excimer laser
Popis výsledku anglicky
In this work, we describe laser modification of poly(methyl methacrylate) films doped with Fast Red ITR, followed by dopant exclusion from the bulk polymer. By this procedure, the polymer can be modified under extremely mild conditions. Creation of surface ordered structure was observed already after application of 15 pulses and 12 mJ cm(-2) fluence. Formation of grating begins in the hottest places and tends to form concentric semi-circles around them. The mechanism of surface ordered structure formation is attributed to polymer ablation, which is more pronounced in the place of higher light intensity. The smoothness of the underlying substrate plays a key role in the quality of surface ordered structure. Most regular grating structures were obtainedon polymer films deposited on atomically 'flat' Si substrates. After laser patterning, the dopant was removed from the polymer by soaking the film in methanol.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JJ - Ostatní materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GBP108%2F12%2FG108" target="_blank" >GBP108/12/G108: Příprava, modifikace a charakterizace materiálů zářením</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2014
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Nanoscale Research Letters
ISSN
1931-7573
e-ISSN
—
Svazek periodika
9
Číslo periodika v rámci svazku
OCT 28 2014
Stát vydavatele periodika
US - Spojené státy americké
Počet stran výsledku
10
Strana od-do
"591.1"-10
Kód UT WoS článku
000347643000003
EID výsledku v databázi Scopus
—