INFLUENCE OF PREPARATION CONDITIONS ON THE MICROSTRUCTURE AND OPTICAL PROPERTIES OF LiNbO3 THIN FILMS
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22310%2F15%3A43899717" target="_blank" >RIV/60461373:22310/15:43899717 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/68378271:_____/15:00451696
Výsledek na webu
<a href="http://www.ceramics-silikaty.cz/2015/pdf/2015_02_164.pdf" target="_blank" >http://www.ceramics-silikaty.cz/2015/pdf/2015_02_164.pdf</a>
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
INFLUENCE OF PREPARATION CONDITIONS ON THE MICROSTRUCTURE AND OPTICAL PROPERTIES OF LiNbO3 THIN FILMS
Popis výsledku v původním jazyce
Thin films of Er3+/Yb3+: LiNbO3 were deposited on sapphire (0001) substrates using a spin-coating process. A deposited solution was prepared by a non-aqueous sol-gel method using 2-methoxyethanol, metallic lithium, niobium(V) ethoxide and erbium and ytterbium acetates. Two starting compositions of LiNbO3 solution (1:1 or congruent) were tested in order to minimize the present of secondary (Er/Yb)NbO4 phases. The effect of different temperature (800 degrees C or 1000 degrees C) and different used atmosphere (air or oxygen) during the films crystallization was also investigated. Rapid annealing (at 1150 degrees C with the heating rate 55 degrees C.s(-1)) was also tested and its influence on secondary phases crystallinity and luminescence of Er3+/Yb3+: LiNbO3 was established. The thin films were characterized by X-ray diffraction analysis, scanning electron microscopy and photoluminescence spectroscopy.
Název v anglickém jazyce
INFLUENCE OF PREPARATION CONDITIONS ON THE MICROSTRUCTURE AND OPTICAL PROPERTIES OF LiNbO3 THIN FILMS
Popis výsledku anglicky
Thin films of Er3+/Yb3+: LiNbO3 were deposited on sapphire (0001) substrates using a spin-coating process. A deposited solution was prepared by a non-aqueous sol-gel method using 2-methoxyethanol, metallic lithium, niobium(V) ethoxide and erbium and ytterbium acetates. Two starting compositions of LiNbO3 solution (1:1 or congruent) were tested in order to minimize the present of secondary (Er/Yb)NbO4 phases. The effect of different temperature (800 degrees C or 1000 degrees C) and different used atmosphere (air or oxygen) during the films crystallization was also investigated. Rapid annealing (at 1150 degrees C with the heating rate 55 degrees C.s(-1)) was also tested and its influence on secondary phases crystallinity and luminescence of Er3+/Yb3+: LiNbO3 was established. The thin films were characterized by X-ray diffraction analysis, scanning electron microscopy and photoluminescence spectroscopy.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CA - Anorganická chemie
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Ceramics-Silikáty
ISSN
0862-5468
e-ISSN
—
Svazek periodika
59
Číslo periodika v rámci svazku
2
Stát vydavatele periodika
CZ - Česká republika
Počet stran výsledku
5
Strana od-do
164-168
Kód UT WoS článku
000362625900012
EID výsledku v databázi Scopus
—