Reaction of soda-lime-silica glass melt with water vapour at melting temperatures

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22310%2F15%3A43900441" target="_blank" >RIV/60461373:22310/15:43900441 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/67985891:_____/15:00450569
Výsledek na webu
<a href="http://dx.doi.org/10.1016/j.jnoncrysol.2015.02.020" target="_blank" >http://dx.doi.org/10.1016/j.jnoncrysol.2015.02.020</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.jnoncrysol.2015.02.020" target="_blank" >10.1016/j.jnoncrysol.2015.02.020</a>

Jazyk výsledku
angličtina
Název v původním jazyce
Reaction of soda-lime-silica glass melt with water vapour at melting temperatures
Popis výsledku v původním jazyce
The soda-lime-silica glass melt was exposed to an atmosphere with a high water vapour partial pressure at temperatures of 1400-1500 oC and the processes in the melt were observed and monitored using the high temperature observation method. The glass batch containing sulfates with carbon - so that the molar ratio between the carbon and sulfate ions in the batch varied between 0 and 9 - the batch without any fining agent and the batch with the addition of antimony oxide were prepared. The foaming and bubble nucleation on the level of the molten glass were observed.
Název v anglickém jazyce
Reaction of soda-lime-silica glass melt with water vapour at melting temperatures
Popis výsledku anglicky
The soda-lime-silica glass melt was exposed to an atmosphere with a high water vapour partial pressure at temperatures of 1400-1500 oC and the processes in the melt were observed and monitored using the high temperature observation method. The glass batch containing sulfates with carbon - so that the molar ratio between the carbon and sulfate ions in the batch varied between 0 and 9 - the batch without any fining agent and the batch with the addition of antimony oxide were prepared. The foaming and bubble nucleation on the level of the molten glass were observed.

Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JH - Keramika, žáruvzdorné materiály a skla
OECD FORD obor
—

Projekt
<a href="/cs/project/TA01010844" target="_blank" >TA01010844: Nová skla a jejich technologie</a><br>
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)