Preparation of Ni-Ti shape memory alloy by spark plasma sintering method

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22310%2F16%3A43902495" target="_blank" >RIV/60461373:22310/16:43902495 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/61389021:_____/16:00473241

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Preparation of Ni-Ti shape memory alloy by spark plasma sintering method

Popis výsledku v původním jazyce

This paper aims to describe powder metallurgy methods of production Ni-Ti shape memory alloy - self-propagating high-temperature synthesis (SHS) and spark plasma sintering (SPS). There are compared microstructures and phase compositions of alloys produced by SHS and by a technology containing SHS, milling and SPS. At the same time there is determined the influence of the SPS sintering temperature on the structure of Ni-Ti alloy. Self-propagating high-temperature synthesis was initiated at 1100 oC with process duration 20 minutes the heating rate of approx. 300 oC/min. The product is highly porous and contains undesirable Ti2Ni phase. The SPS technique allows to obtain product with low porosity. The disadvantages of SPS technique are growing amount of Ti2Ni phase and formation of other undesirable phases (Ni4Ti3 and Ni3Ti).

Název v anglickém jazyce

Preparation of Ni-Ti shape memory alloy by spark plasma sintering method

Popis výsledku anglicky

This paper aims to describe powder metallurgy methods of production Ni-Ti shape memory alloy - self-propagating high-temperature synthesis (SHS) and spark plasma sintering (SPS). There are compared microstructures and phase compositions of alloys produced by SHS and by a technology containing SHS, milling and SPS. At the same time there is determined the influence of the SPS sintering temperature on the structure of Ni-Ti alloy. Self-propagating high-temperature synthesis was initiated at 1100 oC with process duration 20 minutes the heating rate of approx. 300 oC/min. The product is highly porous and contains undesirable Ti2Ni phase. The SPS technique allows to obtain product with low porosity. The disadvantages of SPS technique are growing amount of Ti2Ni phase and formation of other undesirable phases (Ni4Ti3 and Ni3Ti).

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA14-03044S" target="_blank" >GA14-03044S: Příprava slitin NiTi s tvarovou pamětí reaktivní sintrací</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Manufacturing Technology

ISSN

1213-2489

e-ISSN

—

Svazek periodika

16

Číslo periodika v rámci svazku

4

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

5

Strana od-do

804-808

Kód UT WoS článku

—

EID výsledku v databázi Scopus

2-s2.0-84991085193