Effect of nickel particle size on eactive sintering production of NiTi shape memory alloy

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22310%2F16%3A43902525" target="_blank" >RIV/60461373:22310/16:43902525 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Effect of nickel particle size on eactive sintering production of NiTi shape memory alloy

Popis výsledku v původním jazyce

This work is focused on the description of the influence of the particle size of nickel on the synthesis of NiTi shape memory alloy by reactive sintering with high heating rate (300 oC.min-1). It was found that coarse nickel powders undergo only a limited thermally-activated reaction. On the other hand, too fine powders support the low-tempe-rature (500-800 oC) diffusional formation of Ni-Ti intermetallics which could then suppress the rapid thermally-activated reaction. The optimum powder fraction of nickel to obtain the material with the lowest porosity and fraction of undesirable Ti2Ni phase is 25-45 ?m.

Název v anglickém jazyce

Effect of nickel particle size on eactive sintering production of NiTi shape memory alloy

Popis výsledku anglicky

This work is focused on the description of the influence of the particle size of nickel on the synthesis of NiTi shape memory alloy by reactive sintering with high heating rate (300 oC.min-1). It was found that coarse nickel powders undergo only a limited thermally-activated reaction. On the other hand, too fine powders support the low-tempe-rature (500-800 oC) diffusional formation of Ni-Ti intermetallics which could then suppress the rapid thermally-activated reaction. The optimum powder fraction of nickel to obtain the material with the lowest porosity and fraction of undesirable Ti2Ni phase is 25-45 ?m.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA14-03044S" target="_blank" >GA14-03044S: Příprava slitin NiTi s tvarovou pamětí reaktivní sintrací</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Manufacturing Technology

ISSN

1213-2489

e-ISSN

—

Svazek periodika

16

Číslo periodika v rámci svazku

4

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

4

Strana od-do

754-757

Kód UT WoS článku

—

EID výsledku v databázi Scopus

2-s2.0-84991101901