Nanofibers Prepared by Electrospinning from Solutions of Biobased Polyamide 4
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22310%2F17%3A43903863" target="_blank" >RIV/60461373:22310/17:43903863 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/46747885:24410/17:00008803
Výsledek na webu
<a href="http://onlinelibrary.wiley.com/doi/10.1002/pola.28605/full" target="_blank" >http://onlinelibrary.wiley.com/doi/10.1002/pola.28605/full</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1002/pola.28605" target="_blank" >10.1002/pola.28605</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Nanofibers Prepared by Electrospinning from Solutions of Biobased Polyamide 4
Popis výsledku v původním jazyce
A successful preparation of polyamide 4 nanofibers via electrostatic spinning with diameters close to 100 nm is described. Polyamide 4 was prepared by the anionic ringopening polymerization of 2-pyrrolidone and characterized. The effect of the system parameters (i.e., molar mass of the polymer, the solvent system) and the process parameters (i.e., the electrode-to-collector distance) during the electrostatic spinning have been studied. The morphology of the polyamide 4 fiber layers is given except molar mass of the polymer and the concentration of its solution primarily by the conformation of polyamide chains due to polyelectrolyte effect which was confirmed by viscosity measurements.
Název v anglickém jazyce
Nanofibers Prepared by Electrospinning from Solutions of Biobased Polyamide 4
Popis výsledku anglicky
A successful preparation of polyamide 4 nanofibers via electrostatic spinning with diameters close to 100 nm is described. Polyamide 4 was prepared by the anionic ringopening polymerization of 2-pyrrolidone and characterized. The effect of the system parameters (i.e., molar mass of the polymer, the solvent system) and the process parameters (i.e., the electrode-to-collector distance) during the electrostatic spinning have been studied. The morphology of the polyamide 4 fiber layers is given except molar mass of the polymer and the concentration of its solution primarily by the conformation of polyamide chains due to polyelectrolyte effect which was confirmed by viscosity measurements.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
21001 - Nano-materials (production and properties)
Návaznosti výsledku
Projekt
—
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2017
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of polymer science. Part A, Polymer chemistry
ISSN
0887-624X
e-ISSN
—
Svazek periodika
55
Číslo periodika v rámci svazku
13
Stát vydavatele periodika
US - Spojené státy americké
Počet stran výsledku
8
Strana od-do
2203-2210
Kód UT WoS článku
000401192100010
EID výsledku v databázi Scopus
2-s2.0-85017556321