Recovery of Eu and Y from Waste Fluorescent Lamps

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22310%2F17%3A43914127" target="_blank" >RIV/60461373:22310/17:43914127 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Recovery of Eu and Y from Waste Fluorescent Lamps

Popis výsledku v původním jazyce

Eu and Y were extracted from waste fluorescent lamps containing ~0.3% Eu and 7% Y by acidic leaching, hydrolytic precipitation and/or solvent extraction. The leaching tests showed that about 90% Eu and 95% Y were leached in 3M HCl or 3M HNO3 at 80°C, liquid to solid ratio 10:1 in 30 min. Leaching in H2SO4 provided lower Eu and Y extraction efficiency. Only around 85% Eu and 80% Y were extracted at temperatures higher than 70°C. Eu and Y started precipitating simultaneously at pH 1.5 and the precipitation completed at ~ pH 2. Solvent extraction of Eu and Y from sulfate solutions using D2EHPA is strongly influenced by solution pH. At pH 1.4 about 80% Eu and 100%Y were extracted while at pH 1.16 only 25% Eu was extracted together with 90% Y.

Název v anglickém jazyce

Recovery of Eu and Y from Waste Fluorescent Lamps

Popis výsledku anglicky

Eu and Y were extracted from waste fluorescent lamps containing ~0.3% Eu and 7% Y by acidic leaching, hydrolytic precipitation and/or solvent extraction. The leaching tests showed that about 90% Eu and 95% Y were leached in 3M HCl or 3M HNO3 at 80°C, liquid to solid ratio 10:1 in 30 min. Leaching in H2SO4 provided lower Eu and Y extraction efficiency. Only around 85% Eu and 80% Y were extracted at temperatures higher than 70°C. Eu and Y started precipitating simultaneously at pH 1.5 and the precipitation completed at ~ pH 2. Solvent extraction of Eu and Y from sulfate solutions using D2EHPA is strongly influenced by solution pH. At pH 1.4 about 80% Eu and 100%Y were extracted while at pH 1.16 only 25% Eu was extracted together with 90% Y.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of the Polish Mineral Engineering Society

ISSN

1640-4920

e-ISSN

—

Svazek periodika

39

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

PL - Polská republika

Počet stran výsledku

6

Strana od-do

23-28

Kód UT WoS článku

000407742700005

EID výsledku v databázi Scopus

—