The optimization of sintering conditions for the preparation of Ti-Al-Si alloys

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22310%2F17%3A43915357" target="_blank" >RIV/60461373:22310/17:43915357 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

The optimization of sintering conditions for the preparation of Ti-Al-Si alloys

Popis výsledku v původním jazyce

This work deals with optimization of Spark Plasma Sintering conditions for the preparation of Ti-Al-Si alloys. Ti-Al-Si alloys are appropriate material for high-temperature applications, especially for aerospace and automotive industry. They are characterized by low density, good mechanical properties and resistance against oxidation. Ti-Al-Si alloys were prepared by powder metallurgy using reactive sintering, followed by milling and Spark Plasma Sintering. Preparation of intermetallic compounds is complicated due to high melting points of intermediate phases, the exothermic reaction during their formation and high reactivity of the melt with melting crucible. TiAl10Si20 alloy was prepared by Spark Plasma Sintering under a pressure of 48 MPa and by High Pressure Spark Plasma Sintering under pressure of 6 GPa. The temperature was chosen between 1100 °C and 1204 °C. The porosity of TiAl10Si20 alloy decreases with pressure and with the high pressure also increases the hardness by 200 HV 5. Abrasive wear resistance of TiAl10Si20 alloy is very good

Název v anglickém jazyce

The optimization of sintering conditions for the preparation of Ti-Al-Si alloys

Popis výsledku anglicky

This work deals with optimization of Spark Plasma Sintering conditions for the preparation of Ti-Al-Si alloys. Ti-Al-Si alloys are appropriate material for high-temperature applications, especially for aerospace and automotive industry. They are characterized by low density, good mechanical properties and resistance against oxidation. Ti-Al-Si alloys were prepared by powder metallurgy using reactive sintering, followed by milling and Spark Plasma Sintering. Preparation of intermetallic compounds is complicated due to high melting points of intermediate phases, the exothermic reaction during their formation and high reactivity of the melt with melting crucible. TiAl10Si20 alloy was prepared by Spark Plasma Sintering under a pressure of 48 MPa and by High Pressure Spark Plasma Sintering under pressure of 6 GPa. The temperature was chosen between 1100 °C and 1204 °C. The porosity of TiAl10Si20 alloy decreases with pressure and with the high pressure also increases the hardness by 200 HV 5. Abrasive wear resistance of TiAl10Si20 alloy is very good

Druh

J_SC - Článek v periodiku v databázi SCOPUS

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

<a href="/cs/project/GBP108%2F12%2FG043" target="_blank" >GBP108/12/G043: Mikro- a nanokrystalické materiály s vysokým podílem rozhraní pro moderní strukturní aplikace, biodegradabilní implantáty a uchovávání vodíku</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Manufacturing Technology

ISSN

1213-2489

e-ISSN

—

Svazek periodika

17

Číslo periodika v rámci svazku

4

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

6

Strana od-do

483-488

Kód UT WoS článku

—

EID výsledku v databázi Scopus

2-s2.0-85029553385