High-temperature behaviour of Ti-Al-Si alloys prepared by Spark Plasma Sintering
Popis výsledku v původním jazyce
Nowadays, there is effort to substitute in aerospace industry so far commonly used alloys (especially nickel alloys) with new low-density materials, which will have comparable mechanical properties and good resistance against high-temperature oxidation. Ti-Al intermetallic alloys are in this trend modern, already-used material. The results of the tests show that further enhancement of properties can be achieved by addition of silicon. The disadvantage of these materials is a low fracture toughness at room temperature and difficult production. Powder metallurgy seems to be a way to replace still used melting metallurgy. In this work, cyclic oxidation of Ti-Al-Si alloys prepared by reactive sintering, milling and Spark Plasma Sintering is described. The TiAl10Si30 alloy was evaluated as the best alloy from tested ones, because was the most resistant to the stresses. Stress was induced into the oxide layer by repeated annealing and cooling.
Název v anglickém jazyce
High-temperature behaviour of Ti-Al-Si alloys prepared by Spark Plasma Sintering
Popis výsledku anglicky
Nowadays, there is effort to substitute in aerospace industry so far commonly used alloys (especially nickel alloys) with new low-density materials, which will have comparable mechanical properties and good resistance against high-temperature oxidation. Ti-Al intermetallic alloys are in this trend modern, already-used material. The results of the tests show that further enhancement of properties can be achieved by addition of silicon. The disadvantage of these materials is a low fracture toughness at room temperature and difficult production. Powder metallurgy seems to be a way to replace still used melting metallurgy. In this work, cyclic oxidation of Ti-Al-Si alloys prepared by reactive sintering, milling and Spark Plasma Sintering is described. The TiAl10Si30 alloy was evaluated as the best alloy from tested ones, because was the most resistant to the stresses. Stress was induced into the oxide layer by repeated annealing and cooling.
Klasifikace
Druh
J<sub>SC</sub> - Článek v periodiku v databázi SCOPUS
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
<a href="/cs/project/GBP108%2F12%2FG043" target="_blank" >GBP108/12/G043: Mikro- a nanokrystalické materiály s vysokým podílem rozhraní pro moderní strukturní aplikace, biodegradabilní implantáty a uchovávání vodíku</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2017
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Manufacturing Technology
ISSN
1213-2489
e-ISSN
—
Svazek periodika
17
Číslo periodika v rámci svazku
5
Stát vydavatele periodika
CZ - Česká republika
Počet stran výsledku
6
Strana od-do
733-738
Kód UT WoS článku
—
EID výsledku v databázi Scopus
2-s2.0-85030526737