Identification of defects of surface ceramic finishing
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22310%2F19%3A43918070" target="_blank" >RIV/60461373:22310/19:43918070 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Identification of defects of surface ceramic finishing
Popis výsledku v původním jazyce
The main reason of using surface coatings is, in addition to aesthetic requirements, an increase of the resistance of the surface in corrosive environments. Glazes may be applied to various types of ceramic substrates i.e. chemical reactors, dental implants, ceramic whiteware and tiles, porcelain, insulators, ceramic roofing etc. All these products are expected to be highly resistant to various types of degradation processes such as corrosion by environment or thermal stresses developed during production or usage. Defect formation is the main and the most obvious sign of all these undesirable changes of the ceramic body - surface finishing system. The measurement of thermal expansions of contemporary and historical glaze - ceramic body systems by several types of thermal analyses confirmed that the obtained data are suitable for the calculation of stress relations in real glazed ceramic products. The most common types of historical glaze defects were caused by poor system selection or improper storage conditions.
Název v anglickém jazyce
Identification of defects of surface ceramic finishing
Popis výsledku anglicky
The main reason of using surface coatings is, in addition to aesthetic requirements, an increase of the resistance of the surface in corrosive environments. Glazes may be applied to various types of ceramic substrates i.e. chemical reactors, dental implants, ceramic whiteware and tiles, porcelain, insulators, ceramic roofing etc. All these products are expected to be highly resistant to various types of degradation processes such as corrosion by environment or thermal stresses developed during production or usage. Defect formation is the main and the most obvious sign of all these undesirable changes of the ceramic body - surface finishing system. The measurement of thermal expansions of contemporary and historical glaze - ceramic body systems by several types of thermal analyses confirmed that the obtained data are suitable for the calculation of stress relations in real glazed ceramic products. The most common types of historical glaze defects were caused by poor system selection or improper storage conditions.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20506 - Coating and films
Návaznosti výsledku
Projekt
<a href="/cs/project/DG18P02OVV028" target="_blank" >DG18P02OVV028: Technologie ošetření a identifikace degradačních procesů keramických nálezů z hradčanských paláců - Metody restaurování a konzervování pórovité i slinuté keramiky a porcelánu</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2019
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Proceedings of the XIIIth International Conference Preparation of Ceramic Materials
ISBN
978-80-553-3314-4
ISSN
—
e-ISSN
—
Počet stran výsledku
5
Strana od-do
89-93
Název nakladatele
Technická univerzita v Košiciach
Místo vydání
Košice
Místo konání akce
Jahodná
Datum konání akce
25. 6. 2019
Typ akce podle státní příslušnosti
EUR - Evropská akce
Kód UT WoS článku
—