Temperature dependence of Young’s modulus and damping of fused cast AZS materials measured via high-temperature impulse excitation

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22310%2F23%3A43928648" target="_blank" >RIV/60461373:22310/23:43928648 - isvavai.cz</a>

Výsledek na webu

<a href="https://paginas.fe.up.pt/~icem20/proceedings_icem20/" target="_blank" >https://paginas.fe.up.pt/~icem20/proceedings_icem20/</a>

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Temperature dependence of Young’s modulus and damping of fused cast AZS materials measured via high-temperature impulse excitation

Popis výsledku v původním jazyce

The impulse excitation technique (IET) is used to determine Young’s modulus and dampingfor commercial non-refractory alumina-zirconia-silica (AZS) materials containing zircon. Thetemperature dependence of Young’s modulus shows a steep decrease around 900 °C (duringheating) and a sharp minimum at 1000 °C, after which it increases again. The subsequent steepincrease above 1000 °C and the hysteresis during cooling show that this elastic anomaly isrelated to the monoclinic-to-tetragonal phase transition of zirconia. The temperaturedependence of damping shows a distinct damping peak in the range 300–400 °C, which is alsotypical for zirconia, and a steep increase in damping above 700–800 °C, which is lower thanthe onset of the steep Young’s modulus decrease by approximately 100 °C and does not exhibitany hysteresis. This high-temperature damping peak may be affected by the softening behaviorof a small amount of intergranular glass phase.

Název v anglickém jazyce

Temperature dependence of Young’s modulus and damping of fused cast AZS materials measured via high-temperature impulse excitation

Popis výsledku anglicky

The impulse excitation technique (IET) is used to determine Young’s modulus and dampingfor commercial non-refractory alumina-zirconia-silica (AZS) materials containing zircon. Thetemperature dependence of Young’s modulus shows a steep decrease around 900 °C (duringheating) and a sharp minimum at 1000 °C, after which it increases again. The subsequent steepincrease above 1000 °C and the hysteresis during cooling show that this elastic anomaly isrelated to the monoclinic-to-tetragonal phase transition of zirconia. The temperaturedependence of damping shows a distinct damping peak in the range 300–400 °C, which is alsotypical for zirconia, and a steep increase in damping above 700–800 °C, which is lower thanthe onset of the steep Young’s modulus decrease by approximately 100 °C and does not exhibitany hysteresis. This high-temperature damping peak may be affected by the softening behaviorof a small amount of intergranular glass phase.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20504 - Ceramics

Projekt

<a href="/cs/project/GA22-25562S" target="_blank" >GA22-25562S: Impulzní excitace jako nekonvenční metoda k monitorování fázových přeměn a mikrostrukturních změn během tepelného zatížení materiálů</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2023

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proceedings ICEM20

ISBN

978-989-54-7567-4

ISSN

—

e-ISSN

—

Počet stran výsledku

10

Strana od-do

325-334

Název nakladatele

INEGI-FEUP

Místo vydání

Porto

Místo konání akce

Porto

Datum konání akce

2. 7. 2023

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—