Exfoliation of oxide layers and scanning of acoustic emission during tensile testing of steel 304

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22320%2F14%3A43898123" target="_blank" >RIV/60461373:22320/14:43898123 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Exfoliation of oxide layers and scanning of acoustic emission during tensile testing of steel 304

Popis výsledku v původním jazyce

The aim of this contribution was to evaluate the oxide layers created on construction materials of steam superheater. Main degrading problem of superheaters is exfoliation of oxide layers and clogging pipes, reducing diameter of pipes. Moreover exfoliated material is entrained directly on turbine where corrosion and disruption of surface of rotor blades occure. Significant effect of exfoliation is energy loss. The base material is stainless steel 1.4301, (AISI 304) where main alloying elements are: chrome (18% Cr) forming a chromium oxide layer, nickel (10% Ni) and carbon under 0,03%. There is desirable to create protective chromium oxide layer instead of fragile magnetite layer.

Název v anglickém jazyce

Exfoliation of oxide layers and scanning of acoustic emission during tensile testing of steel 304

Popis výsledku anglicky

The aim of this contribution was to evaluate the oxide layers created on construction materials of steam superheater. Main degrading problem of superheaters is exfoliation of oxide layers and clogging pipes, reducing diameter of pipes. Moreover exfoliated material is entrained directly on turbine where corrosion and disruption of surface of rotor blades occure. Significant effect of exfoliation is energy loss. The base material is stainless steel 1.4301, (AISI 304) where main alloying elements are: chrome (18% Cr) forming a chromium oxide layer, nickel (10% Ni) and carbon under 0,03%. There is desirable to create protective chromium oxide layer instead of fragile magnetite layer.

Druh

D - Stať ve sborníku

CEP obor

CI - Průmyslová chemie a chemické inženýrství

OECD FORD obor

—

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Low emission technologies conference

ISBN

978-80-01-05665-3

ISSN

—

e-ISSN

—

Počet stran výsledku

5

Strana od-do

52-56

Název nakladatele

České vysoké učení technické v Praze

Místo vydání

Praha

Místo konání akce

Praha

Datum konání akce

27. 11. 2014

Typ akce podle státní příslušnosti

CST - Celostátní akce

Kód UT WoS článku

—