In-situ electrochemical study of Zr1Nb alloy corrosion in high temerature Li+ containing water

Popis výsledku v původním jazyce

Long-term in-situ corrosion tests were performed in order to evaluate the influence of lithium ions on the corrosion of zirconium alloy. Experiments were carried out in a high-pressure high-temperature loop (280 oC, 8 MPa) in a high concentration water solution of LiOH (70 and 200 ppm Li+) and in a simulated WWER primary coolant environment. The kinetic parameters characterizing the oxidation process have been explored using in-situ electrochemical impedance spectroscopy and slow potentiodynamic polarization. The Mott-Schottky approach was used to determine the semiconducting character of the passive film.

Název v anglickém jazyce

In-situ electrochemical study of Zr1Nb alloy corrosion in high temerature Li+ containing water

Popis výsledku anglicky

Long-term in-situ corrosion tests were performed in order to evaluate the influence of lithium ions on the corrosion of zirconium alloy. Experiments were carried out in a high-pressure high-temperature loop (280 oC, 8 MPa) in a high concentration water solution of LiOH (70 and 200 ppm Li+) and in a simulated WWER primary coolant environment. The kinetic parameters characterizing the oxidation process have been explored using in-situ electrochemical impedance spectroscopy and slow potentiodynamic polarization. The Mott-Schottky approach was used to determine the semiconducting character of the passive film.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JF - Jaderná energetika

OECD FORD obor

—

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach<br>I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of nuclear materials

ISSN

0022-3115

e-ISSN

—

Svazek periodika

467

Číslo periodika v rámci svazku

December 2015

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

9

Strana od-do

302-310

Kód UT WoS článku

000309799100022

EID výsledku v databázi Scopus

—