Synthesis of MnO, Mn2O3 and Mn3O4 nanocrystal clusters by thermal decomposition of manganese glycerolate
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22330%2F15%3A43897450" target="_blank" >RIV/60461373:22330/15:43897450 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/60461373:22310/15:43897450
Výsledek na webu
<a href="http://www.sciencedirect.com/science/article/pii/S0272884214013455" target="_blank" >http://www.sciencedirect.com/science/article/pii/S0272884214013455</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.ceramint.2014.08.108" target="_blank" >10.1016/j.ceramint.2014.08.108</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Synthesis of MnO, Mn2O3 and Mn3O4 nanocrystal clusters by thermal decomposition of manganese glycerolate
Popis výsledku v původním jazyce
We successfully prepared MnO, Mn2O3 and Mn3O4 nanoparticles by thermal decomposition of manganese (II) glycerolate in air or inert atmosphere at various temperatures. The thermal behavior during decomposition was analyzed by simultaneous thermal analysis. The manganese precursor was analyzed by X-Ray diffraction, SEM, SEM-EDS and X-Ray photoelectron spectroscopy to evaluate exact composition. The particle size of the obtained nanoparticles was determined from XRD patterns using Scherrer equation and also by transmission electron microscopy. Thanks to the extremely low sizes, such nanoparticles can be used at large-scales for industrial use
Název v anglickém jazyce
Synthesis of MnO, Mn2O3 and Mn3O4 nanocrystal clusters by thermal decomposition of manganese glycerolate
Popis výsledku anglicky
We successfully prepared MnO, Mn2O3 and Mn3O4 nanoparticles by thermal decomposition of manganese (II) glycerolate in air or inert atmosphere at various temperatures. The thermal behavior during decomposition was analyzed by simultaneous thermal analysis. The manganese precursor was analyzed by X-Ray diffraction, SEM, SEM-EDS and X-Ray photoelectron spectroscopy to evaluate exact composition. The particle size of the obtained nanoparticles was determined from XRD patterns using Scherrer equation and also by transmission electron microscopy. Thanks to the extremely low sizes, such nanoparticles can be used at large-scales for industrial use
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CA - Anorganická chemie
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA13-17538S" target="_blank" >GA13-17538S: Oxidové termoelektrické materiály pro konverzi vysokoteplotního odpadního tepla</a><br>
Návaznosti
S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Ceramics International
ISSN
0272-8842
e-ISSN
—
Svazek periodika
41
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
BE - Belgické království
Počet stran výsledku
7
Strana od-do
595-601
Kód UT WoS článku
000346216300071
EID výsledku v databázi Scopus
—