Elektrochemická Vizualizace Daktyloskopických Stop

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22340%2F23%3A43927113" target="_blank" >RIV/60461373:22340/23:43927113 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/60461373:22810/23:43927113
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
čeština
Název v původním jazyce
Elektrochemická Vizualizace Daktyloskopických Stop
Popis výsledku v původním jazyce
This study is focused on the visualization of fingerprints with electropolymerized poly(neutral red) (PNR) on metal surfaces including cartridges. Polymer film was prepared from 2 mM NR using cyclic voltammetry in phosphate buffer with 0.1M KNO3 on brass substrates in potential range −0.20–0.50 V (vs. Ag/AgCl) at a scan rate of 50 mV s−1 for 6–10 cycles. The morphology and structure of modified surfaces with fingerprints and PNR were studied. This perspective way to visualize latent fingerprints with observed details of the papillary lines could be applied for future in forensic practice.
Název v anglickém jazyce
Electrochemical Visualization of Dactyloscopic Traces
Popis výsledku anglicky
This study is focused on the visualization of fingerprints with electropolymerized poly(neutral red) (PNR) on metal surfaces including cartridges. Polymer film was prepared from 2 mM NR using cyclic voltammetry in phosphate buffer with 0.1M KNO3 on brass substrates in potential range −0.20–0.50 V (vs. Ag/AgCl) at a scan rate of 50 mV s−1 for 6–10 cycles. The morphology and structure of modified surfaces with fingerprints and PNR were studied. This perspective way to visualize latent fingerprints with observed details of the papillary lines could be applied for future in forensic practice.

Projekt
<a href="/cs/project/VK01010022" target="_blank" >VK01010022: Pokročilé metody vizualizace daktyloskopických stop</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění
2023
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)