Role of steel and zinc coating thickness in cut edge corrosion of coil coated materials in atmospheric weathering conditions; Part 1: Laboratory study
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22350%2F16%3A43902759" target="_blank" >RIV/60461373:22350/16:43902759 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1016/j.porgcoat.2016.06.013" target="_blank" >http://dx.doi.org/10.1016/j.porgcoat.2016.06.013</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.porgcoat.2016.06.013" target="_blank" >10.1016/j.porgcoat.2016.06.013</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Role of steel and zinc coating thickness in cut edge corrosion of coil coated materials in atmospheric weathering conditions; Part 1: Laboratory study
Popis výsledku v původním jazyce
Cathode surface area and its ability to reduce oxygen controlled the rate of zinc dissolution and paint delamination from cut edges of hot dip galvanised steel sheets. Zinc corrosion products deposited on steel in atmospheric exposure conditions inhibited oxygen reduction decreasing galvanic current and zinc dissolution and paint delamination. The opposite effect was observed for iron corrosion products. The initial steel substrate and zinc coating thicknesses affected the availability of zinc ions for formation of the protective film.
Název v anglickém jazyce
Role of steel and zinc coating thickness in cut edge corrosion of coil coated materials in atmospheric weathering conditions; Part 1: Laboratory study
Popis výsledku anglicky
Cathode surface area and its ability to reduce oxygen controlled the rate of zinc dissolution and paint delamination from cut edges of hot dip galvanised steel sheets. Zinc corrosion products deposited on steel in atmospheric exposure conditions inhibited oxygen reduction decreasing galvanic current and zinc dissolution and paint delamination. The opposite effect was observed for iron corrosion products. The initial steel substrate and zinc coating thicknesses affected the availability of zinc ions for formation of the protective film.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JK - Koroze a povrchové úpravy materiálu
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
N - Vyzkumna aktivita podporovana z neverejnych zdroju
Ostatní
Rok uplatnění
2016
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Progress in Organic Coating
ISSN
0300-9440
e-ISSN
—
Svazek periodika
99
Číslo periodika v rámci svazku
October 2016
Stát vydavatele periodika
NL - Nizozemsko
Počet stran výsledku
14
Strana od-do
"356?364"
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—