Mechanism of Carbon Steel Corrosion in Accelerated Corrosion Tests
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22350%2F25%3A43933783" target="_blank" >RIV/60461373:22350/25:43933783 - isvavai.cz</a>
Výsledek na webu
<a href="https://onlinelibrary.wiley.com/doi/10.1002/maco.202414606" target="_blank" >https://onlinelibrary.wiley.com/doi/10.1002/maco.202414606</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1002/maco.202414606" target="_blank" >10.1002/maco.202414606</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Mechanism of Carbon Steel Corrosion in Accelerated Corrosion Tests
Popis výsledku v původním jazyce
Understanding the effect of parameters of cyclic accelerated corrosion tests on the corrosion response is crucial for proper test design. The real-time corrosion rate of carbon steel was measured using electrical resistance sensors in seven tests and was statistically evaluated. A synergistic effect of the chloride concentration and duration of transition phases was explained based on the surface electrolyte distribution. In contrast to the field, the steel corrosion rate increased between particular chloride deposition phases due to the formation of porous red rust with low protection ability. This implies that the corrosivity of future corrosion tests needs to be reduced.
Název v anglickém jazyce
Mechanism of Carbon Steel Corrosion in Accelerated Corrosion Tests
Popis výsledku anglicky
Understanding the effect of parameters of cyclic accelerated corrosion tests on the corrosion response is crucial for proper test design. The real-time corrosion rate of carbon steel was measured using electrical resistance sensors in seven tests and was statistically evaluated. A synergistic effect of the chloride concentration and duration of transition phases was explained based on the surface electrolyte distribution. In contrast to the field, the steel corrosion rate increased between particular chloride deposition phases due to the formation of porous red rust with low protection ability. This implies that the corrosivity of future corrosion tests needs to be reduced.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
20500 - Materials engineering
Návaznosti výsledku
Projekt
<a href="/cs/project/FW01010482" target="_blank" >FW01010482: Vývoj zařízení pro měření korozivity atmosféry</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2025
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION
ISSN
0947-5117
e-ISSN
1521-4176
Svazek periodika
76
Číslo periodika v rámci svazku
4
Stát vydavatele periodika
DE - Spolková republika Německo
Počet stran výsledku
24
Strana od-do
486-509
Kód UT WoS článku
001391887300001
EID výsledku v databázi Scopus
—