Preparation of Nanosized Micro/Mesoporous Composites.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61388955%3A_____%2F03%3A54030230" target="_blank" >RIV/61388955:_____/03:54030230 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Preparation of Nanosized Micro/Mesoporous Composites.

Popis výsledku v původním jazyce

Micro/mesoporous composite material is prepared via reaction of zeolite Beta seeds solution and mesoporous precursor solution under hydrothermal conditions. The resulted micro/mesoporous composite contains nanoparticles with a mean radius of about 90 nm,while pure zeolite Beta and MCM-41 have particles with size of about 50 nm and 230 nm, respectively. The presence of highly crosslinked silicon framework walls and tetrahedrally coordinated aluminum in the framework structure are confirmed with solid-state 29Si and 27Al NMR investigations. Adsorption measurements show the presence of micropores, mesopores and high interparticle porosity due to the nanometer-sized particles in the micro/mesoporous composite. Various techniques such as dynamic light scattering, scanning electron.

Název v anglickém jazyce

Preparation of Nanosized Micro/Mesoporous Composites.

Popis výsledku anglicky

Micro/mesoporous composite material is prepared via reaction of zeolite Beta seeds solution and mesoporous precursor solution under hydrothermal conditions. The resulted micro/mesoporous composite contains nanoparticles with a mean radius of about 90 nm,while pure zeolite Beta and MCM-41 have particles with size of about 50 nm and 230 nm, respectively. The presence of highly crosslinked silicon framework walls and tetrahedrally coordinated aluminum in the framework structure are confirmed with solid-state 29Si and 27Al NMR investigations. Adsorption measurements show the presence of micropores, mesopores and high interparticle porosity due to the nanometer-sized particles in the micro/mesoporous composite. Various techniques such as dynamic light scattering, scanning electron.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CF - Fyzikální chemie a teoretická chemie

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2003

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials Science and Engineering. C

ISSN

0928-4931

e-ISSN

—

Svazek periodika

23

Číslo periodika v rámci svazku

N/A

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

5

Strana od-do

1001-1005

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—