Struktura a stabilita geopolymérů syntetizovaných ze zbytkových kaolinů a lupkových jílů

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61388955%3A_____%2F05%3A00031114" target="_blank" >RIV/61388955:_____/05:00031114 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/62243136:_____/05:20

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Structure and stability of geopolymers synthesized from kaolinitic and shale clay residues

Popis výsledku v původním jazyce

Calcined kaolin ans shale clay residues from textile filter were utilized to synthesis of geopolymers with molar Si/Al ration ranging from 3 to 4 with sodium and potassium silicates with modulus 1.20-1.66. The properties of aluminosilicate residues, polymerization process, structure and stability of resulting products in water and mineral acid were analyzed using FTIR, MAS-NMR, XRD and SEM techniques. It was found that geopolymers prepared from calcined shale clay residues with sand as filter exhibitedhigh values of compressive (up to 100 MPa) and flexural (up to 15 MPa) strength even after immersion of samples after curing process in water. Relationship was found between development of local structure, polymerization degree and compressive strength,however FTIR and Al and Si period.

Název v anglickém jazyce

Structure and stability of geopolymers synthesized from kaolinitic and shale clay residues

Popis výsledku anglicky

Calcined kaolin ans shale clay residues from textile filter were utilized to synthesis of geopolymers with molar Si/Al ration ranging from 3 to 4 with sodium and potassium silicates with modulus 1.20-1.66. The properties of aluminosilicate residues, polymerization process, structure and stability of resulting products in water and mineral acid were analyzed using FTIR, MAS-NMR, XRD and SEM techniques. It was found that geopolymers prepared from calcined shale clay residues with sand as filter exhibitedhigh values of compressive (up to 100 MPa) and flexural (up to 15 MPa) strength even after immersion of samples after curing process in water. Relationship was found between development of local structure, polymerization degree and compressive strength,however FTIR and Al and Si period.

Druh

D - Stať ve sborníku

CEP obor

CF - Fyzikální chemie a teoretická chemie

OECD FORD obor

—

Projekt

<a href="/cs/project/FI-IM%2F079" target="_blank" >FI-IM/079: *Využití zbytkových a odpadních hlinitokřemičitanů pro výrobu stavebních hmot na bázi anorganických polymerů.</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2005

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Geopolymer, Green Chemistry and Sustainable Development Solutions

ISBN

2-9514820-0-0

ISSN

—

e-ISSN

—

Počet stran výsledku

4

Strana od-do

81-84

Název nakladatele

Institut Géopolymere

Místo vydání

Saint-Quentin

Místo konání akce

Saint-Quentin

Datum konání akce

1. 1. 2005

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—