Vliv velikosti částic na elektrokatalytickou aktivitu nanokrystalických RuO2 elektrod
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61388955%3A_____%2F06%3A00032534" target="_blank" >RIV/61388955:_____/06:00032534 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Particle size dependence of the electrocatalytic activity of nanocrystalline RuO2 electrodes
Popis výsledku v původním jazyce
The effect of nanocrystal size/shape on the electrocatalytic behavior of nanocrystalline oxide electrodes was demonstrated on electrodes based on sol-gel-prepared RuO2 materials. The typical particle size ranged between 15 and 40 nm. Regardless of the particle size, the nanocrystals were of isometric shape with polygonal prismatic part capped with two pyramids. The prismatic part of the nanocrystals featured {110}- and {100}-oriented faces in the case of small nanocrystals (d < 20 nm) and {110}, {100} and {140} in the case of bigger nanocrystals (d > 20 nm). The pyramidal parts were formed by {101}-oriented faces. The activity of the RuO2 nanocrystals towards oxygen evolution reaction decreases with increasing particle size; the activity towards chlorine evolution is insensitive to the particle size/shape. The observed tendency indicates that the oxygen evolution is significantly affected by the crystal edges while chlorine evolution reaction proceeds mainly on crystal faces.
Název v anglickém jazyce
Particle size dependence of the electrocatalytic activity of nanocrystalline RuO2 electrodes
Popis výsledku anglicky
The effect of nanocrystal size/shape on the electrocatalytic behavior of nanocrystalline oxide electrodes was demonstrated on electrodes based on sol-gel-prepared RuO2 materials. The typical particle size ranged between 15 and 40 nm. Regardless of the particle size, the nanocrystals were of isometric shape with polygonal prismatic part capped with two pyramids. The prismatic part of the nanocrystals featured {110}- and {100}-oriented faces in the case of small nanocrystals (d < 20 nm) and {110}, {100} and {140} in the case of bigger nanocrystals (d > 20 nm). The pyramidal parts were formed by {101}-oriented faces. The activity of the RuO2 nanocrystals towards oxygen evolution reaction decreases with increasing particle size; the activity towards chlorine evolution is insensitive to the particle size/shape. The observed tendency indicates that the oxygen evolution is significantly affected by the crystal edges while chlorine evolution reaction proceeds mainly on crystal faces.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CG - Elektrochemie
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/1ET400400413" target="_blank" >1ET400400413: Vývoj programového prostředí pro matematické simulace a predikce v katalýze a elektrokatalýze</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2006
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of the Electrochemical Society
ISSN
0013-4651
e-ISSN
—
Svazek periodika
153
Číslo periodika v rámci svazku
6
Stát vydavatele periodika
US - Spojené státy americké
Počet stran výsledku
8
Strana od-do
"E111"-"E118"
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—