Fotoelektrické vlastnosti prášků dopovaného sulfidu kademnatého
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61388955%3A_____%2F06%3A00041692" target="_blank" >RIV/61388955:_____/06:00041692 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Photoelectrical properties of doped cadmium sulphide powders
Popis výsledku v původním jazyce
Photosensitive powders of CdS were prepared with different concentrations of dopants. Doses of donors (Cl-) and acceptors (Cu2+, Ag+) varied from 0 to 41 and from 0 to 9 mg/g CdS, respectively. Reflectance, absorption coefficient and resistance dependence on illumination intensity and voltage at the wavelength of about .lambda. = 630 nm and photovoltage spectra in the range 450-900 nm were measured on layers prepared from the powders. The value of absorption coefficient grew with the increasing dopant concentrations; acceptors appeared more efficient than donors. Reflectance decreased with growing acceptor dose. Using the values of reflectance, absorption coefficient and resistance the corrected photovoltage, as the measure of the concentration photogenerated charge carriers, was calculated. The ratio (.sigma.IGB) of the corrected photovoltage and photocurrent was used as the criterion of intergrain barrier conductivity. ...
Název v anglickém jazyce
Photoelectrical properties of doped cadmium sulphide powders
Popis výsledku anglicky
Photosensitive powders of CdS were prepared with different concentrations of dopants. Doses of donors (Cl-) and acceptors (Cu2+, Ag+) varied from 0 to 41 and from 0 to 9 mg/g CdS, respectively. Reflectance, absorption coefficient and resistance dependence on illumination intensity and voltage at the wavelength of about .lambda. = 630 nm and photovoltage spectra in the range 450-900 nm were measured on layers prepared from the powders. The value of absorption coefficient grew with the increasing dopant concentrations; acceptors appeared more efficient than donors. Reflectance decreased with growing acceptor dose. Using the values of reflectance, absorption coefficient and resistance the corrected photovoltage, as the measure of the concentration photogenerated charge carriers, was calculated. The ratio (.sigma.IGB) of the corrected photovoltage and photocurrent was used as the criterion of intergrain barrier conductivity. ...
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CF - Fyzikální chemie a teoretická chemie
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/FT-TA2%2F018" target="_blank" >FT-TA2/018: Pokročilé svazkové technologie vytváření a zpracování vrstev pro výrobní praxi v elektronice.</a><br>
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2006
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Solar Energy Materials and Solar Cells
ISSN
0927-0248
e-ISSN
—
Svazek periodika
90
Číslo periodika v rámci svazku
17
Stát vydavatele periodika
NL - Nizozemsko
Počet stran výsledku
10
Strana od-do
2924-2933
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—