Mesoporézní silika modifikovaná aminopropylovými ligandy: Vliv velikosti pórů na zachycování oxidu uhličitého

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61388955%3A_____%2F08%3A00312182" target="_blank" >RIV/61388955:_____/08:00312182 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/61388980:_____/08:00312182

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Amine-modified ordered mesoporous silica: Effect of pore size on carbon dioxide capture

Popis výsledku v původním jazyce

Three mesoporous silica materials with different pore sizes (33 A for small pore size MCM-41; 38 A for SBA-12; 71 A for large pore size SBA-15) and pore connectivity (2D for MCM-41 and SBA-15-type materials; 3D for SBA-12 material) were prepared and functionalized with aminopropyl (AP) ligands by post-synthesis treatment. The materials were characterized by small angle X-ray scattering (SAXS), transmission electron microscopy (TEM), thermogravimetric analysis (TGA) and nitrogen adsorption/desorption experiments. The carbon dioxide sorption on modified mesoporous molecular sieves was investigated by using of microbalances at 25 °C, and the influence of pore size and pore architecture on CO2 sorption was discussed. The large pore silica, SBA-15, showed the largest carbon dioxide sorption capacity (1.5 mmol/g), relating to highest amine surface density in this material.

Název v anglickém jazyce

Amine-modified ordered mesoporous silica: Effect of pore size on carbon dioxide capture

Popis výsledku anglicky

Three mesoporous silica materials with different pore sizes (33 A for small pore size MCM-41; 38 A for SBA-12; 71 A for large pore size SBA-15) and pore connectivity (2D for MCM-41 and SBA-15-type materials; 3D for SBA-12 material) were prepared and functionalized with aminopropyl (AP) ligands by post-synthesis treatment. The materials were characterized by small angle X-ray scattering (SAXS), transmission electron microscopy (TEM), thermogravimetric analysis (TGA) and nitrogen adsorption/desorption experiments. The carbon dioxide sorption on modified mesoporous molecular sieves was investigated by using of microbalances at 25 °C, and the influence of pore size and pore architecture on CO2 sorption was discussed. The large pore silica, SBA-15, showed the largest carbon dioxide sorption capacity (1.5 mmol/g), relating to highest amine surface density in this material.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CF - Fyzikální chemie a teoretická chemie

OECD FORD obor

—

Projekt

<a href="/cs/project/GA203%2F08%2F0604" target="_blank" >GA203/08/0604: Pokročilé materiály na bázi molekulových sít pro adsorpci a uchovávání CO2 a H2</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Chemical Engineering Journal

ISSN

1385-8947

e-ISSN

—

Svazek periodika

144

Číslo periodika v rámci svazku

2

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

7

Strana od-do

—

Kód UT WoS článku

000260451500023

EID výsledku v databázi Scopus

—