Cesta ke kompositním membránám typu MFI zeolit- .alpha.-alumina pro separaci lehkých parafinů

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61388955%3A_____%2F08%3A00315645" target="_blank" >RIV/61388955:_____/08:00315645 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/60461373:22310/08:00020023

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

A route to MFI zeolite-.alpha.-alumina composite membranes for separation of light paraffins

Popis výsledku v původním jazyce

Zeolites are microporous crystalline materials used as catalysts, ion-exchangers, adsorbents and molecular sieves. Several industrial separation processes, e.g. dehydration of alcohols, have been developed based on zeolite membranes. It is also of greatinterest the separation of light paraffins. Silicalite-1 crystal layers were synthesised on the surface of asymmetric .alpha.-alumina planar supports. A molar ratio of synthesis mixture was 100 SiO2:42.9 TPAOH: 2229 H2O with Aerosil 380 (Degussa) used asa silica source. Permeation and separation characteristics of the membranes were measured using steady state apparatus MEMFIS. Separation factor of ceramic silicalite-1 composite membrane, which was synthesised for 24 h using a synthesis mixture aged for 7 days, was studied by an equimolar mixture of butane isomers as a function of temperature. High separation factor for n-butane (>10) in the mixture with isobutane showed good quality of the composite membrane.

Název v anglickém jazyce

A route to MFI zeolite-.alpha.-alumina composite membranes for separation of light paraffins

Popis výsledku anglicky

Zeolites are microporous crystalline materials used as catalysts, ion-exchangers, adsorbents and molecular sieves. Several industrial separation processes, e.g. dehydration of alcohols, have been developed based on zeolite membranes. It is also of greatinterest the separation of light paraffins. Silicalite-1 crystal layers were synthesised on the surface of asymmetric .alpha.-alumina planar supports. A molar ratio of synthesis mixture was 100 SiO2:42.9 TPAOH: 2229 H2O with Aerosil 380 (Degussa) used asa silica source. Permeation and separation characteristics of the membranes were measured using steady state apparatus MEMFIS. Separation factor of ceramic silicalite-1 composite membrane, which was synthesised for 24 h using a synthesis mixture aged for 7 days, was studied by an equimolar mixture of butane isomers as a function of temperature. High separation factor for n-butane (>10) in the mixture with isobutane showed good quality of the composite membrane.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CF - Fyzikální chemie a teoretická chemie

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Desalination

ISSN

0011-9164

e-ISSN

—

Svazek periodika

224

Číslo periodika v rámci svazku

1-3

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

5

Strana od-do

—

Kód UT WoS článku

000255606800015

EID výsledku v databázi Scopus

—