Nanobubble-assisted formation of carbon nanostructures on basal plane highly ordered pyrolytic graphite exposed to aqueous media
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61388955%3A_____%2F10%3A00341532" target="_blank" >RIV/61388955:_____/10:00341532 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/61388980:_____/10:00341532
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Nanobubble-assisted formation of carbon nanostructures on basal plane highly ordered pyrolytic graphite exposed to aqueous media
Popis výsledku v původním jazyce
Ambient gas nanobubbles of size similar to 10(1)-10(2) nm occupying the hydrophobic surface of basal plane highly ordered pyrolytic graphite (HOPG) immersed in aqueous media at room temperature cause exfoliation of the top graphene layers, as revealed byboth in situ and ex situ atomic force microscope (AFM) imaging. The formation of nanoparticles composed mostly from graphene-based nanoscrolls, nanohorn-like and onion-like nanostructures was resolved by high resolution transmission electron microscopy(TEM) and examined by diffraction and x-ray photoelectron spectroscopy (XPS) analyses. The diameter of nanostructures varied from about 5 nm for single-layered scrolls to tens of nanometres for multishells. Raman spectroscopy confirmed the structural rearrangement of the HOPG basal plane after the above-mentioned treatment. The implications for nanobubble interfacial forces are discussed.
Název v anglickém jazyce
Nanobubble-assisted formation of carbon nanostructures on basal plane highly ordered pyrolytic graphite exposed to aqueous media
Popis výsledku anglicky
Ambient gas nanobubbles of size similar to 10(1)-10(2) nm occupying the hydrophobic surface of basal plane highly ordered pyrolytic graphite (HOPG) immersed in aqueous media at room temperature cause exfoliation of the top graphene layers, as revealed byboth in situ and ex situ atomic force microscope (AFM) imaging. The formation of nanoparticles composed mostly from graphene-based nanoscrolls, nanohorn-like and onion-like nanostructures was resolved by high resolution transmission electron microscopy(TEM) and examined by diffraction and x-ray photoelectron spectroscopy (XPS) analyses. The diameter of nanostructures varied from about 5 nm for single-layered scrolls to tens of nanometres for multishells. Raman spectroscopy confirmed the structural rearrangement of the HOPG basal plane after the above-mentioned treatment. The implications for nanobubble interfacial forces are discussed.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CF - Fyzikální chemie a teoretická chemie
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Nanotechnology
ISSN
0957-4484
e-ISSN
—
Svazek periodika
21
Číslo periodika v rámci svazku
9
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
7
Strana od-do
—
Kód UT WoS článku
000274360300032
EID výsledku v databázi Scopus
—