Impact of Parent Zirconia Crystallinity/Amorphicity on the n-heptane Isomerization over Pt/WO3-ZrO2 Catalysts
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61388955%3A_____%2F15%3A00444884" target="_blank" >RIV/61388955:_____/15:00444884 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/62243136:_____/15:MPO05CL
Výsledek na webu
<a href="http://dx.doi.org/10.9734/BJAST/2015/18557" target="_blank" >http://dx.doi.org/10.9734/BJAST/2015/18557</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.9734/BJAST/2015/18557" target="_blank" >10.9734/BJAST/2015/18557</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Impact of Parent Zirconia Crystallinity/Amorphicity on the n-heptane Isomerization over Pt/WO3-ZrO2 Catalysts
Popis výsledku v původním jazyce
A series of WO3-ZrO2 catalysts containing 18% of WO3 were prepared from Zr(OH)4 pre-calcined at temperatures between 25 to 700°C, before W-introduction by impregnation. Thus, in accordance with that, the resulting parent Zr(OH)4 support possessed different degree of crystallinity and proportion of monoclinic to tetrahedral (M/T) phases which directly influenced the same M/T ratio in the final Pt/WO3-ZrO2 catalyst. The resulting catalysts varied in nuclearity and reducibility of formed WOx species, as revealed by UV-Vis spectroscopy and TPR-H2. Despite widely different surface area of the final catalysts, ranged from 140 to 47 m2/g, related to the proportion of M/T phases, ranged from 10%/90% to 90%/10%; the activity of the corresponding Pt/WO3-ZrO2 forisomerization of C7 was found to be directly proportional only to the total surface area of the resulting catalysts without specific effect of the crystal modifications of the support. In accordance with that a correlation was observed b
Název v anglickém jazyce
Impact of Parent Zirconia Crystallinity/Amorphicity on the n-heptane Isomerization over Pt/WO3-ZrO2 Catalysts
Popis výsledku anglicky
A series of WO3-ZrO2 catalysts containing 18% of WO3 were prepared from Zr(OH)4 pre-calcined at temperatures between 25 to 700°C, before W-introduction by impregnation. Thus, in accordance with that, the resulting parent Zr(OH)4 support possessed different degree of crystallinity and proportion of monoclinic to tetrahedral (M/T) phases which directly influenced the same M/T ratio in the final Pt/WO3-ZrO2 catalyst. The resulting catalysts varied in nuclearity and reducibility of formed WOx species, as revealed by UV-Vis spectroscopy and TPR-H2. Despite widely different surface area of the final catalysts, ranged from 140 to 47 m2/g, related to the proportion of M/T phases, ranged from 10%/90% to 90%/10%; the activity of the corresponding Pt/WO3-ZrO2 forisomerization of C7 was found to be directly proportional only to the total surface area of the resulting catalysts without specific effect of the crystal modifications of the support. In accordance with that a correlation was observed b
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CF - Fyzikální chemie a teoretická chemie
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/FR-TI3%2F316" target="_blank" >FR-TI3/316: *Výzkum a vývoj katalyzátoru na bázi oxidu zirkoničitého a jeho aplikace pro izomeraci C5 a C6 uhlovodíkové frakce</a><br>
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
British Journal of Applied Science & Technology
ISSN
2231-0843
e-ISSN
—
Svazek periodika
10
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
15
Strana od-do
—
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—