Self-templating synthesis of hollow spheres of zeolite ZSM-5 from spray-dried aluminosilicate precursor

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61388955%3A_____%2F16%3A00458867" target="_blank" >RIV/61388955:_____/16:00458867 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/62243136:_____/16:N0000028

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.micromeso.2016.03.021" target="_blank" >http://dx.doi.org/10.1016/j.micromeso.2016.03.021</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.micromeso.2016.03.021" target="_blank" >10.1016/j.micromeso.2016.03.021</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Self-templating synthesis of hollow spheres of zeolite ZSM-5 from spray-dried aluminosilicate precursor

Popis výsledku v původním jazyce

Synthesis of hollow spheres consisting of ZSM-5 zeolite crystals, prepared by a cost- and time-saving self-templating process, requires neither a hard/soft template for sphere formation nor tetraalkylammonium compound as a zeolite structure-directing agent. A preshaped aluminosilicate precursor, obtained by spray drying of a mixture of colloidal solution of silicic acid and aluminum butoxide, plays the role of a shape-directing agent for the formation of spheres, and is used as a source of silica and alumina for zeolite growth. The zeolite structure is directed using ZSM-5 seeds. This method yielded highly stable hollow spheres with diameters of 15–25 μm, consisting of inter-grown ZSM-5 crystals (Si/Al 14) with a size of 0.5–2.0 μm.

Název v anglickém jazyce

Self-templating synthesis of hollow spheres of zeolite ZSM-5 from spray-dried aluminosilicate precursor

Popis výsledku anglicky

Synthesis of hollow spheres consisting of ZSM-5 zeolite crystals, prepared by a cost- and time-saving self-templating process, requires neither a hard/soft template for sphere formation nor tetraalkylammonium compound as a zeolite structure-directing agent. A preshaped aluminosilicate precursor, obtained by spray drying of a mixture of colloidal solution of silicic acid and aluminum butoxide, plays the role of a shape-directing agent for the formation of spheres, and is used as a source of silica and alumina for zeolite growth. The zeolite structure is directed using ZSM-5 seeds. This method yielded highly stable hollow spheres with diameters of 15–25 μm, consisting of inter-grown ZSM-5 crystals (Si/Al 14) with a size of 0.5–2.0 μm.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CF - Fyzikální chemie a teoretická chemie

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Microporous and Mesoporous Materials

ISSN

1387-1811

e-ISSN

—

Svazek periodika

228

Číslo periodika v rámci svazku

JUL 2016

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

5

Strana od-do

59-63

Kód UT WoS článku

000376805700008

EID výsledku v databázi Scopus

2-s2.0-84977610308