Thermal behavior of Fe2O3/TiO2 mesoporous gels
Popis výsledku v původním jazyce
Titania-based photocatalytic materials were prepared by sol - gel method using Fe3+ and polyethyleneglycol (PEG(600)) as additives. Thermogravimetry (TG), differential thermal analysis (DTA) and evolved gas analysis (EGA) with MS detection were used to elucidate processes that take place during heating of Fe3+ containing titania gels. The microstructure development of the Fe2O3/TiO2 gel samples with and without PEG(600) admixtures was characterized by emanation thermal analysis ( ETA) under in situ heating in air. A mathematical model was used for the evaluation of ETA results. Surface area and porosity measurements of the samples dried at 120 &DEG; C and the samples preheated for 1 h to 300 and 500 &DEG; C were compared. From the XRD measurements it was confirmed that the crystallization of anatase took place after thermal heating up to 600 &DEG; C.
Název v anglickém jazyce
Thermal behavior of Fe2O3/TiO2 mesoporous gels
Popis výsledku anglicky
Titania-based photocatalytic materials were prepared by sol - gel method using Fe3+ and polyethyleneglycol (PEG(600)) as additives. Thermogravimetry (TG), differential thermal analysis (DTA) and evolved gas analysis (EGA) with MS detection were used to elucidate processes that take place during heating of Fe3+ containing titania gels. The microstructure development of the Fe2O3/TiO2 gel samples with and without PEG(600) admixtures was characterized by emanation thermal analysis ( ETA) under in situ heating in air. A mathematical model was used for the evaluation of ETA results. Surface area and porosity measurements of the samples dried at 120 &DEG; C and the samples preheated for 1 h to 300 and 500 &DEG; C were compared. From the XRD measurements it was confirmed that the crystallization of anatase took place after thermal heating up to 600 &DEG; C.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CA - Anorganická chemie
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2005
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of Thermal Analysis and Calorimetry: an international forum for thermal studies
ISSN
1388-6150
e-ISSN
—
Svazek periodika
80
Číslo periodika v rámci svazku
2
Stát vydavatele periodika
HU - Maďarsko
Počet stran výsledku
7
Strana od-do
503-509
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—