Kinetic studies on leucite precursors

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61388980%3A_____%2F09%3A00340094" target="_blank" >RIV/61388980:_____/09:00340094 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/60461373:22310/09:00022478

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Kinetic studies on leucite precursors

Popis výsledku v původním jazyce

Kinetic studies were performed on two types of leucite precursors. These precursors were prepared using a hydrothermal method at 150 degrees C; the reaction time was 1.5 hours. In order to obtain precursors having different amounts of seed the molarity of KOH was changed. These intermediate products were subsequently calcinated from 5 minutes to 72 hours at temperatures of 850 degrees C, 900 degrees C, 950 degrees C, 1000 degrees C and 1050 degrees C. The crystallinities of the powders were calculated by X-ray diffraction analysis. The crystallization curves for the synthesis of leucite exhibited a typical sigmoidal characteristic. Using different kinetic equations it was found that the Avrami-Erofeev model is the most appropriate to describe the experimental data. Using the Avrami-Erofeev model n reaches an average value of 2.9 which is connected with the three-dimensional growth of nuclei.

Název v anglickém jazyce

Kinetic studies on leucite precursors

Popis výsledku anglicky

Kinetic studies were performed on two types of leucite precursors. These precursors were prepared using a hydrothermal method at 150 degrees C; the reaction time was 1.5 hours. In order to obtain precursors having different amounts of seed the molarity of KOH was changed. These intermediate products were subsequently calcinated from 5 minutes to 72 hours at temperatures of 850 degrees C, 900 degrees C, 950 degrees C, 1000 degrees C and 1050 degrees C. The crystallinities of the powders were calculated by X-ray diffraction analysis. The crystallization curves for the synthesis of leucite exhibited a typical sigmoidal characteristic. Using different kinetic equations it was found that the Avrami-Erofeev model is the most appropriate to describe the experimental data. Using the Avrami-Erofeev model n reaches an average value of 2.9 which is connected with the three-dimensional growth of nuclei.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/2A-1TP1%2F063" target="_blank" >2A-1TP1/063: Nové skelné a keramické materiály a pokročilé postupy jejich příprav a výrob.</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Central European Journal of Chemistry

ISSN

1895-1066

e-ISSN

—

Svazek periodika

7

Číslo periodika v rámci svazku

2

Stát vydavatele periodika

PL - Polská republika

Počet stran výsledku

6

Strana od-do

—

Kód UT WoS článku

000265019100009

EID výsledku v databázi Scopus

—