High surface area alpha-alumina preparation by using urban waste

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61388980%3A_____%2F09%3A00341292" target="_blank" >RIV/61388980:_____/09:00341292 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

High surface area alpha-alumina preparation by using urban waste

Popis výsledku v původním jazyce

A new method for preparing high surface area a-alumina from urban waste is proposed. The method consists of the precipitation of a precursor that contains bohemite mixed with a linear polymer and subsequently the thermal decomposition of the precursor byheating in nitrogen and air to 1200 degrees C. The resulting a-alumina consists of nanocrystals of about 100 nm aggregated into larger particles with relatively high surface area (12 m(2) g(-1)) and a significant macropore volume of 0.545 cm(3) g. Methods of X-ray diffraction (XRD), scanning electron microscopy (SEM), high-resolution transmission electron microscopy (HRTEM) and selected area electron diffraction (SAED) were used to characterize microstructure of prepared materials. Results of differential thermal analysis, thermogravimetry and emanation thermal analysis characterized the thermal behaviour of alpha-alumina precursors.

Název v anglickém jazyce

High surface area alpha-alumina preparation by using urban waste

Popis výsledku anglicky

A new method for preparing high surface area a-alumina from urban waste is proposed. The method consists of the precipitation of a precursor that contains bohemite mixed with a linear polymer and subsequently the thermal decomposition of the precursor byheating in nitrogen and air to 1200 degrees C. The resulting a-alumina consists of nanocrystals of about 100 nm aggregated into larger particles with relatively high surface area (12 m(2) g(-1)) and a significant macropore volume of 0.545 cm(3) g. Methods of X-ray diffraction (XRD), scanning electron microscopy (SEM), high-resolution transmission electron microscopy (HRTEM) and selected area electron diffraction (SAED) were used to characterize microstructure of prepared materials. Results of differential thermal analysis, thermogravimetry and emanation thermal analysis characterized the thermal behaviour of alpha-alumina precursors.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CA - Anorganická chemie

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Ceramics International

ISSN

0272-8842

e-ISSN

—

Svazek periodika

35

Číslo periodika v rámci svazku

6

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

7

Strana od-do

—

Kód UT WoS článku

000267387500002

EID výsledku v databázi Scopus

—