Synthesis of mesoporous titania by homogeneous hydrolysis of titania oxo-sulfate in the presence of cationic and anionic surfactants
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61388980%3A_____%2F10%3A00356667" target="_blank" >RIV/61388980:_____/10:00356667 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Synthesis of mesoporous titania by homogeneous hydrolysis of titania oxo-sulfate in the presence of cationic and anionic surfactants
Popis výsledku v původním jazyce
Mesoporous titania was prepared by homogeneous hydrolysis of titanium oxo-sulphate with urea in aqueous solutions in the presence of the cationic and anionic surfactants, cetyl trimethyl ammonium bromide (CTAB) and sodium dodecyl benzene sulfonate (SDBS), respectively. Following annealing at 600°C the structure of prepared samples was determined with X-ray powder diffraction (XRD) and selected area electron diffraction (SAED). The morphology and microstructure characteristics were also obtained by scanning electron microscopy (SEM) and high resolution electron microscopy (HRTEM). Surface area (BET) and porosity were also determined. The prepared mesoporous titania samples showed considerably higher photocatalytic activity compared to reference samplesprepared without surfactants and with P25 Degussa.
Název v anglickém jazyce
Synthesis of mesoporous titania by homogeneous hydrolysis of titania oxo-sulfate in the presence of cationic and anionic surfactants
Popis výsledku anglicky
Mesoporous titania was prepared by homogeneous hydrolysis of titanium oxo-sulphate with urea in aqueous solutions in the presence of the cationic and anionic surfactants, cetyl trimethyl ammonium bromide (CTAB) and sodium dodecyl benzene sulfonate (SDBS), respectively. Following annealing at 600°C the structure of prepared samples was determined with X-ray powder diffraction (XRD) and selected area electron diffraction (SAED). The morphology and microstructure characteristics were also obtained by scanning electron microscopy (SEM) and high resolution electron microscopy (HRTEM). Surface area (BET) and porosity were also determined. The prepared mesoporous titania samples showed considerably higher photocatalytic activity compared to reference samplesprepared without surfactants and with P25 Degussa.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CA - Anorganická chemie
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA203%2F08%2F0334" target="_blank" >GA203/08/0334: Fotokatalytické materiály pro destrukci bojových otravných látek</a><br>
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Ceramics - Silikáty
ISSN
0862-5468
e-ISSN
—
Svazek periodika
54
Číslo periodika v rámci svazku
4
Stát vydavatele periodika
CZ - Česká republika
Počet stran výsledku
11
Strana od-do
—
Kód UT WoS článku
000286027800013
EID výsledku v databázi Scopus
—