Highly photoactive 2D titanium dioxide nanostructures prepared from lyophilized aqueous colloids of peroxo-polytitanic acid
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61388980%3A_____%2F14%3A00429129" target="_blank" >RIV/61388980:_____/14:00429129 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1016/j.materresbull.2013.09.028" target="_blank" >http://dx.doi.org/10.1016/j.materresbull.2013.09.028</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.materresbull.2013.09.028" target="_blank" >10.1016/j.materresbull.2013.09.028</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Highly photoactive 2D titanium dioxide nanostructures prepared from lyophilized aqueous colloids of peroxo-polytitanic acid
Popis výsledku v původním jazyce
Reaction of hydrogen peroxide with suspensions of thoroughly washed precipitates obtained by neutralization of aqueous solution of titanyl sulfate with aqueous ammonia leads to transparent yellow liquids. In this way prepared colloid solution is a two phase system in which, beyond the water phase, also a liquid hydrated peroxo-polytitanic acid component is present. Freeze drying of this colloid liquid provides a foamy material consisting of thin foils of peroxo-polytitanic acid containing small but notnegligible amount of chemically bound ammonia. These foams annealed at temperature above similar to 200 degrees C lose water, ammonia and excess of oxygen providing foamy amorphous oxide. At higher temperatures above similar to 280 degrees C the amorphous material crystallizes to anatase which transforms at temperatures >850 degrees C to rutile. The size and shape of the initial leaflets forming the foam is preserved up to similar to 900 degrees C. Slit shaped porosity is formed during a
Název v anglickém jazyce
Highly photoactive 2D titanium dioxide nanostructures prepared from lyophilized aqueous colloids of peroxo-polytitanic acid
Popis výsledku anglicky
Reaction of hydrogen peroxide with suspensions of thoroughly washed precipitates obtained by neutralization of aqueous solution of titanyl sulfate with aqueous ammonia leads to transparent yellow liquids. In this way prepared colloid solution is a two phase system in which, beyond the water phase, also a liquid hydrated peroxo-polytitanic acid component is present. Freeze drying of this colloid liquid provides a foamy material consisting of thin foils of peroxo-polytitanic acid containing small but notnegligible amount of chemically bound ammonia. These foams annealed at temperature above similar to 200 degrees C lose water, ammonia and excess of oxygen providing foamy amorphous oxide. At higher temperatures above similar to 280 degrees C the amorphous material crystallizes to anatase which transforms at temperatures >850 degrees C to rutile. The size and shape of the initial leaflets forming the foam is preserved up to similar to 900 degrees C. Slit shaped porosity is formed during a
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CA - Anorganická chemie
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA203%2F09%2F1117" target="_blank" >GA203/09/1117: Příprava fotokatalyzátorů na bázi Ti/O/Si laserovou depozicí z plynné fáze a sol-gel technikou</a><br>
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2014
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Materials Research Bulletin
ISSN
0025-5408
e-ISSN
—
Svazek periodika
49
Číslo periodika v rámci svazku
JAN
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
8
Strana od-do
405-412
Kód UT WoS článku
000330081400063
EID výsledku v databázi Scopus
—