Crystallization processes in Ge2Sb2Se4Te glass
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61388980%3A_____%2F15%3A00438948" target="_blank" >RIV/61388980:_____/15:00438948 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/00216275:25310/15:39898715
Výsledek na webu
<a href="http://dx.doi.org/10.1016/j.materresbull.2014.10.032" target="_blank" >http://dx.doi.org/10.1016/j.materresbull.2014.10.032</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.materresbull.2014.10.032" target="_blank" >10.1016/j.materresbull.2014.10.032</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Crystallization processes in Ge2Sb2Se4Te glass
Popis výsledku v původním jazyce
Differential scanning calorimetry (DSC) and X-ray diffraction (XRD) analysis were used to study crystallization in Ge2Sb2Se4Te glass under non-isothermal conditions as a function of the particle size. The crystallization kinetics was described in terms of the autocatalytic Šesták-Berggren model. An extensive discussion of all aspects of a full-scale kinetic study of a crystallization process was undertaken. Dominance of the crystallization process originating from mechanically induced strains and heterogeneities was confirmed. Substitution of Se by Te was found to enhance the manifestation of the bulk crystallization mechanisms (at the expense of surface crystallization). The XRD analysis showed significant dependence of the crystalline structural parameters on the crystallization conditions (initial particle size of the glassy grains and applied heating rate). Based on this information, a new microstructural crystallization mechanism, indistinguishable by DSC, was proposed.
Název v anglickém jazyce
Crystallization processes in Ge2Sb2Se4Te glass
Popis výsledku anglicky
Differential scanning calorimetry (DSC) and X-ray diffraction (XRD) analysis were used to study crystallization in Ge2Sb2Se4Te glass under non-isothermal conditions as a function of the particle size. The crystallization kinetics was described in terms of the autocatalytic Šesták-Berggren model. An extensive discussion of all aspects of a full-scale kinetic study of a crystallization process was undertaken. Dominance of the crystallization process originating from mechanically induced strains and heterogeneities was confirmed. Substitution of Se by Te was found to enhance the manifestation of the bulk crystallization mechanisms (at the expense of surface crystallization). The XRD analysis showed significant dependence of the crystalline structural parameters on the crystallization conditions (initial particle size of the glassy grains and applied heating rate). Based on this information, a new microstructural crystallization mechanism, indistinguishable by DSC, was proposed.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CA - Anorganická chemie
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GAP106%2F11%2F1152" target="_blank" >GAP106/11/1152: Reverzibilní krystalizace a strukturni relaxace amorfních materiálů pro záznam informace</a><br>
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Materials Research Bulletin
ISSN
0025-5408
e-ISSN
—
Svazek periodika
61
Číslo periodika v rámci svazku
JAN
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
8
Strana od-do
207-214
Kód UT WoS článku
000347498700035
EID výsledku v databázi Scopus
—