Determination of gamma solution temperature in Re-rich Ni-base superalloy by small-angle neutron scattering.
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389005%3A_____%2F01%3A49010110" target="_blank" >RIV/61389005:_____/01:49010110 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Determination of gamma solution temperature in Re-rich Ni-base superalloy by small-angle neutron scattering.
Popis výsledku v původním jazyce
A harmful segregation of heavy elements (e.g. W, Mo, Re) during solidification of Ni-base superalloys can only be eliminated by using a homogenizing heat treatment, which needs to be carried out in the single-phase (gamma) field above the gamma solvus temperature but below the solidus temperature. Small-angle neutron scattering (SANS) was employed for in situ observation of the dissolution of precipitation in an Re-rich superalloy. The temperature dependence of the relative volume fraction and the sizedistribution of smaller gamma precipitates, and the specific surface of large inhomogeneities as well as some other parameters were determined from the two dimensional scattering curves measured for as-cast and heat-treated samples.
Název v anglickém jazyce
Determination of gamma solution temperature in Re-rich Ni-base superalloy by small-angle neutron scattering.
Popis výsledku anglicky
A harmful segregation of heavy elements (e.g. W, Mo, Re) during solidification of Ni-base superalloys can only be eliminated by using a homogenizing heat treatment, which needs to be carried out in the single-phase (gamma) field above the gamma solvus temperature but below the solidus temperature. Small-angle neutron scattering (SANS) was employed for in situ observation of the dissolution of precipitation in an Re-rich superalloy. The temperature dependence of the relative volume fraction and the sizedistribution of smaller gamma precipitates, and the specific surface of large inhomogeneities as well as some other parameters were determined from the two dimensional scattering curves measured for as-cast and heat-treated samples.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BG - Jaderná, atomová a molekulová fyzika, urychlovače
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2001
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of Applied Crystallography
ISSN
0021-8898
e-ISSN
—
Svazek periodika
34
Číslo periodika v rámci svazku
N/A
Stát vydavatele periodika
DK - Dánské království
Počet stran výsledku
8
Strana od-do
541-548
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—