In situ neutron diffraction during tensile straining of fine grained ferrite-pearlite steel

Popis výsledku v původním jazyce

Situ neutron diffraction during tensile deformation was performed on a steel with ferrite grain size 3.6 mum, which was close to the achievable minimum size for a ferrite-pearlite structure. The lattice plane strain, microstrain related to dislocation density, and the size of coherently diffracting blocks related to dislocation cell size were determined from the profile analysis of (110) diffraction spectra, as a function of the applied stress. The change in lattice plane strain revealed that grain refining strongly influences 'grain to grain yielding' behaviour with respect to Luders deformation. The increase in dislocation density estimated in the uniformly extending regime was similar to that observed in another specimen with ferrite grain size 46.2mum

Název v anglickém jazyce

In situ neutron diffraction during tensile straining of fine grained ferrite-pearlite steel

Popis výsledku anglicky

Situ neutron diffraction during tensile deformation was performed on a steel with ferrite grain size 3.6 mum, which was close to the achievable minimum size for a ferrite-pearlite structure. The lattice plane strain, microstrain related to dislocation density, and the size of coherently diffracting blocks related to dislocation cell size were determined from the profile analysis of (110) diffraction spectra, as a function of the applied stress. The change in lattice plane strain revealed that grain refining strongly influences 'grain to grain yielding' behaviour with respect to Luders deformation. The increase in dislocation density estimated in the uniformly extending regime was similar to that observed in another specimen with ferrite grain size 46.2mum

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials Science and Technology

ISSN

0267-0836

e-ISSN

—

Svazek periodika

20

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

5

Strana od-do

121-125

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—