Diffusion of 6Li in Ta and W

Popis výsledku v původním jazyce

The objective of this work was the study of 6Li diffusion in the Ta and W refractory metals. The samples were prepared by ion implantation of 380 keV 6Li ions into W and Ta thin foils (up to the fluence of 1E16 ions/cm2) and annealed up to the temperature 1940 C. The depth profiles of 6Li were determined using the Thermal Neutron Depth Profiling (TNDP) technique. The results showed that diffusion of 6Li in both W and Ta foils is very complex and cannot be described by simple Fick?s laws. Trapping centers (in the subsurface layers of both W and Ta metals) were supposed in a trial to explain the 6Li diffusion behavior. However, the 6Li depth profiles were only partly explained. Other aspects are necessary to take into account for more proper quantification; such as spatially dependent diffusion coefficients, etc.

Název v anglickém jazyce

Diffusion of 6Li in Ta and W

Popis výsledku anglicky

The objective of this work was the study of 6Li diffusion in the Ta and W refractory metals. The samples were prepared by ion implantation of 380 keV 6Li ions into W and Ta thin foils (up to the fluence of 1E16 ions/cm2) and annealed up to the temperature 1940 C. The depth profiles of 6Li were determined using the Thermal Neutron Depth Profiling (TNDP) technique. The results showed that diffusion of 6Li in both W and Ta foils is very complex and cannot be described by simple Fick?s laws. Trapping centers (in the subsurface layers of both W and Ta metals) were supposed in a trial to explain the 6Li diffusion behavior. However, the 6Li depth profiles were only partly explained. Other aspects are necessary to take into account for more proper quantification; such as spatially dependent diffusion coefficients, etc.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Nuclear Instruments and Methods in Physical Research. B

ISSN

0168-583X

e-ISSN

—

Svazek periodika

249

Číslo periodika v rámci svazku

1-2

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

4

Strana od-do

865-868

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—