Studium dusíkaté martenzitické oceli 0Kh16N4AB při zátěži pomocí neutronové difrakce

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389005%3A_____%2F08%3A00322456" target="_blank" >RIV/61389005:_____/08:00322456 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Neutron diffraction study of a nitrogen martensitic steel 0Kh16N4AB under load

Popis výsledku v původním jazyce

An austenitic-martensitic nitrogen steel 0Kh16N4AB has been studied under load using high-resolution neutron diffraction analysis on an FSD neutron diffractometer at an IBR-2 reactor (Dubna) and on a diffractometer with a focusing monochromator on a reactor of the Nuclear Physics Institute (Czech Republic). Young's moduli calculated from different reflections of the martensite and austenite phases have been obtained. It has been found that the yield strength sigma(0.2) corresponding to the slip plane (111) of the austenite phase is anomalously low and that with increasing degree of uniaxial tension the width of lines (111)(gamma) strongly grows. In the steel under consideration the plane (111) of the austenite phase appears to be an easy-slip plane that ensures the enhanced properties of the steel, i.e., the combination of a high ultimate strength (1600 MPa) with a high plasticity (delta = 16%).

Název v anglickém jazyce

Neutron diffraction study of a nitrogen martensitic steel 0Kh16N4AB under load

Popis výsledku anglicky

An austenitic-martensitic nitrogen steel 0Kh16N4AB has been studied under load using high-resolution neutron diffraction analysis on an FSD neutron diffractometer at an IBR-2 reactor (Dubna) and on a diffractometer with a focusing monochromator on a reactor of the Nuclear Physics Institute (Czech Republic). Young's moduli calculated from different reflections of the martensite and austenite phases have been obtained. It has been found that the yield strength sigma(0.2) corresponding to the slip plane (111) of the austenite phase is anomalously low and that with increasing degree of uniaxial tension the width of lines (111)(gamma) strongly grows. In the steel under consideration the plane (111) of the austenite phase appears to be an easy-slip plane that ensures the enhanced properties of the steel, i.e., the combination of a high ultimate strength (1600 MPa) with a high plasticity (delta = 16%).

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BG - Jaderná, atomová a molekulová fyzika, urychlovače

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Physics of Metals and Metallography

ISSN

0031-918X

e-ISSN

—

Svazek periodika

105

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

RU - Ruská federace

Počet stran výsledku

4

Strana od-do

—

Kód UT WoS článku

000253527300009

EID výsledku v databázi Scopus

—