Investigation of phase transformations by in-situ neutron diffraction in a Co-Re-based high temperature alloy
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389005%3A_____%2F10%3A00351180" target="_blank" >RIV/61389005:_____/10:00351180 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/26722445:_____/10:#0000560
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Investigation of phase transformations by in-situ neutron diffraction in a Co-Re-based high temperature alloy
Popis výsledku v původním jazyce
In-situ neutron diffraction at high temperatures was used to investigate phase transformation in a Co-Re-based alloy. Stability of carbides and transformation of Co matrix from epsilon (hcp) to gamma (fcc) phase were studied. The epsilon = gamma phase transformation exhibited a large hysteresis with temperature. The alloy has a complex microstructure with Cr23C6. TaC and sigma phase stable over a wide temperature range. The hysteresis is the result of composition interplay between Co-matrix and other phases, e.g. Cr-carbide and sigma. TaC is stable at high temperatures up to 1300 degrees C.
Název v anglickém jazyce
Investigation of phase transformations by in-situ neutron diffraction in a Co-Re-based high temperature alloy
Popis výsledku anglicky
In-situ neutron diffraction at high temperatures was used to investigate phase transformation in a Co-Re-based alloy. Stability of carbides and transformation of Co matrix from epsilon (hcp) to gamma (fcc) phase were studied. The epsilon = gamma phase transformation exhibited a large hysteresis with temperature. The alloy has a complex microstructure with Cr23C6. TaC and sigma phase stable over a wide temperature range. The hysteresis is the result of composition interplay between Co-matrix and other phases, e.g. Cr-carbide and sigma. TaC is stable at high temperatures up to 1300 degrees C.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BG - Jaderná, atomová a molekulová fyzika, urychlovače
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Materials Letters
ISSN
0167-577X
e-ISSN
—
Svazek periodika
64
Číslo periodika v rámci svazku
23
Stát vydavatele periodika
NL - Nizozemsko
Počet stran výsledku
4
Strana od-do
—
Kód UT WoS článku
000283968900014
EID výsledku v databázi Scopus
—