NANOSTRUCTURE CHARACTERIZATION OF IN738LC SUPERALLOY FATIGUED AT HIGH TEMPERATURE

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389005%3A_____%2F13%3A00399770" target="_blank" >RIV/61389005:_____/13:00399770 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68081723:_____/13:00399770 RIV/00216305:26210/13:PU110102

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

NANOSTRUCTURE CHARACTERIZATION OF IN738LC SUPERALLOY FATIGUED AT HIGH TEMPERATURE

Popis výsledku v původním jazyce

The nanostructure of Inconel 738LC Ni-superalloy strengthened by trimodal γ’ precipitates distribution was investigated after Low Cycle Fatigue (LCF) loading at temperature 700°C. Different microscopic techniques as Scanning Electron Microscope (SEM) equipped with STEM detector, transmission Kikuchi diffraction in the SEM, transmission electron microscope (TEM) in the bright field mode and high resolution transmission electron microscopes in STEM mode were used for the characterization of nanostructure. The characteristic morphology of γ’ precipitates was examined by ex-situ and in-situ Small Angle Neutron Scattering (SANS) at high temperatures. All microscopic techniques indicate that the morphology of γ’ precipitates distributed in the γ matrix as received state corresponds to two types, i.e. large cuboid-like precipitates with the size around 670 nm, and the spherical precipitates with the diameter 52 nm. After the LCF tests at temperature 700°C, the ex-situ SANS measurement yielded additional scattering intensities coming from another small γ’ precipitates with estimated size up to 10 nm.

Název v anglickém jazyce

NANOSTRUCTURE CHARACTERIZATION OF IN738LC SUPERALLOY FATIGUED AT HIGH TEMPERATURE

Popis výsledku anglicky

The nanostructure of Inconel 738LC Ni-superalloy strengthened by trimodal γ’ precipitates distribution was investigated after Low Cycle Fatigue (LCF) loading at temperature 700°C. Different microscopic techniques as Scanning Electron Microscope (SEM) equipped with STEM detector, transmission Kikuchi diffraction in the SEM, transmission electron microscope (TEM) in the bright field mode and high resolution transmission electron microscopes in STEM mode were used for the characterization of nanostructure. The characteristic morphology of γ’ precipitates was examined by ex-situ and in-situ Small Angle Neutron Scattering (SANS) at high temperatures. All microscopic techniques indicate that the morphology of γ’ precipitates distributed in the γ matrix as received state corresponds to two types, i.e. large cuboid-like precipitates with the size around 670 nm, and the spherical precipitates with the diameter 52 nm. After the LCF tests at temperature 700°C, the ex-situ SANS measurement yielded additional scattering intensities coming from another small γ’ precipitates with estimated size up to 10 nm.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20306 - Audio engineering, reliability analysis

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2013

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

NANOCON 2013 Conference Proceedings

ISBN

978-80-87294-44-4

ISSN

—

e-ISSN

—

Počet stran výsledku

7

Strana od-do

"art. no. 2001"

Název nakladatele

Tanger

Místo vydání

Ostrava

Místo konání akce

Brno

Datum konání akce

16. 10. 2013

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

000352070900127