Monotonic and cyclic properties of TiAl alloys doped with Nb, Mo and C

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389005%3A_____%2F14%3A00434484" target="_blank" >RIV/61389005:_____/14:00434484 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68081723:_____/14:00434484

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.proeng.2014.06.289" target="_blank" >http://dx.doi.org/10.1016/j.proeng.2014.06.289</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.proeng.2014.06.289" target="_blank" >10.1016/j.proeng.2014.06.289</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Monotonic and cyclic properties of TiAl alloys doped with Nb, Mo and C

Popis výsledku v původním jazyce

Six grades of TiAl alloys doped with 7 at.% Nb and variable content of C and/or Mo were studied. The as-received microstructure and phase composition of the alloys was characterized using neutron diffraction experiments and electron microscopy. They aresubstantially different in individual alloys. In Mo containing alloys, ordered 0 phase is present while carbon suppresses the occurrence of this phase. Alternating lamellae of and 2 phases are characteristic for all specimens. The specimens have been subjected to monotonic testing (tensile and compression) and to low cycle fatigue testing at ambient and at elevated temperatures. The differences in microstructure result in scatter of mechanical behaviour of the alloys, e.g. the yield stress at 750°C varies from 445 to 626 MPa. The mechanical properties of the materials are discussed in relation to the initial microstructure and phase composition.

Název v anglickém jazyce

Monotonic and cyclic properties of TiAl alloys doped with Nb, Mo and C

Popis výsledku anglicky

Six grades of TiAl alloys doped with 7 at.% Nb and variable content of C and/or Mo were studied. The as-received microstructure and phase composition of the alloys was characterized using neutron diffraction experiments and electron microscopy. They aresubstantially different in individual alloys. In Mo containing alloys, ordered 0 phase is present while carbon suppresses the occurrence of this phase. Alternating lamellae of and 2 phases are characteristic for all specimens. The specimens have been subjected to monotonic testing (tensile and compression) and to low cycle fatigue testing at ambient and at elevated temperatures. The differences in microstructure result in scatter of mechanical behaviour of the alloys, e.g. the yield stress at 750°C varies from 445 to 626 MPa. The mechanical properties of the materials are discussed in relation to the initial microstructure and phase composition.

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

XVII International Colloquium on Mechanical Fatigue of Metals (ICMFM17)

ISBN

—

ISSN

1877-7058

e-ISSN

—

Počet stran výsledku

4

Strana od-do

405-408

Název nakladatele

Elsevier

Místo vydání

Amsterdam

Místo konání akce

Verbania

Datum konání akce

25. 6. 2014

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—