Influence of multiple small-angle neutron scattering on diffraction peak broadening in ferritic steel
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389005%3A_____%2F15%3A00443879" target="_blank" >RIV/61389005:_____/15:00443879 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1107/S1600576715000813" target="_blank" >http://dx.doi.org/10.1107/S1600576715000813</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1107/S1600576715000813" target="_blank" >10.1107/S1600576715000813</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Influence of multiple small-angle neutron scattering on diffraction peak broadening in ferritic steel
Popis výsledku v původním jazyce
Peak broadening of neutron diffraction was studied at various neutron wavelengths (1.24-2.61 angstrom). As the neutron beam path through a specimen increased, significant peak broadening was observed in ferritic steel, but not in austenitic steel. The peak broadening was reduced under a magnetic field applied perpendicular to the beam direction. Small-angle neutron scattering results showed significant reduction in scattering intensities under a magnetic field of 1.2T. It is suggested that the peak broadening can be attributed to multiple small-angle neutron scattering by magnetic domains. Thus, a sufficiently strong magnetic field could enhance the deep penetration capability of neutron diffraction by reducing the peak broadening.
Název v anglickém jazyce
Influence of multiple small-angle neutron scattering on diffraction peak broadening in ferritic steel
Popis výsledku anglicky
Peak broadening of neutron diffraction was studied at various neutron wavelengths (1.24-2.61 angstrom). As the neutron beam path through a specimen increased, significant peak broadening was observed in ferritic steel, but not in austenitic steel. The peak broadening was reduced under a magnetic field applied perpendicular to the beam direction. Small-angle neutron scattering results showed significant reduction in scattering intensities under a magnetic field of 1.2T. It is suggested that the peak broadening can be attributed to multiple small-angle neutron scattering by magnetic domains. Thus, a sufficiently strong magnetic field could enhance the deep penetration capability of neutron diffraction by reducing the peak broadening.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of Applied Crystallography
ISSN
0021-8898
e-ISSN
—
Svazek periodika
48
Číslo periodika v rámci svazku
APR
Stát vydavatele periodika
US - Spojené státy americké
Počet stran výsledku
7
Strana od-do
350-356
Kód UT WoS článku
000352229100005
EID výsledku v databázi Scopus
2-s2.0-84926300815