Effect of chemical modification on the mechanical properties of plasma-polymerized organosilicones

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389005%3A_____%2F18%3A00490716" target="_blank" >RIV/61389005:_____/18:00490716 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/00216305:26310/18:PU129481

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.porgcoat.2018.02.020" target="_blank" >http://dx.doi.org/10.1016/j.porgcoat.2018.02.020</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.porgcoat.2018.02.020" target="_blank" >10.1016/j.porgcoat.2018.02.020</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Effect of chemical modification on the mechanical properties of plasma-polymerized organosilicones

Popis výsledku v původním jazyce

Plasma-polymerized films of tetravinylsilane or its mixture with oxygen gas were deposited at low effective powers (0.1-10 W) using RF pulsed plasma. The Young's modulus and hardness of the plasma polymer films were characterized by conventional instrumented nanoindentation. Based on a chemical analysis of the deposited films, the chemical modification of the plasma polymer network was responsible for changing the mechanical properties. More cross-linked and stiffer plasma polymer networks resulted in increased mechanical properties of films deposited from pure tetravinylsilane. However, the oxygen atoms from the monomer mixture with oxygen gas resulted in the formation of stronger chemical species but decreased plasma polymer crosslinking that altered the mechanical properties.

Název v anglickém jazyce

Effect of chemical modification on the mechanical properties of plasma-polymerized organosilicones

Popis výsledku anglicky

Plasma-polymerized films of tetravinylsilane or its mixture with oxygen gas were deposited at low effective powers (0.1-10 W) using RF pulsed plasma. The Young's modulus and hardness of the plasma polymer films were characterized by conventional instrumented nanoindentation. Based on a chemical analysis of the deposited films, the chemical modification of the plasma polymer network was responsible for changing the mechanical properties. More cross-linked and stiffer plasma polymer networks resulted in increased mechanical properties of films deposited from pure tetravinylsilane. However, the oxygen atoms from the monomer mixture with oxygen gas resulted in the formation of stronger chemical species but decreased plasma polymer crosslinking that altered the mechanical properties.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20506 - Coating and films

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2018

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Progress in Organic Coatings

ISSN

0300-9440

e-ISSN

—

Svazek periodika

119

Číslo periodika v rámci svazku

6

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

6

Strana od-do

85-90

Kód UT WoS článku

000434754200012

EID výsledku v databázi Scopus

2-s2.0-85042727808