A Study of Progressive Milling Technology on Surface Topography and Fatigue Properties of the High Strength Aluminum Alloy 7475-T7351

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389005%3A_____%2F18%3A00500896" target="_blank" >RIV/61389005:_____/18:00500896 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/00216305:26210/17:PU125664

Výsledek na webu

<a href="http://dx.doi.org/10.1007/978-3-319-70365-7_2" target="_blank" >http://dx.doi.org/10.1007/978-3-319-70365-7_2</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1007/978-3-319-70365-7_2" target="_blank" >10.1007/978-3-319-70365-7_2</a>

Jazyk výsledku

angličtina

Název v původním jazyce

A Study of Progressive Milling Technology on Surface Topography and Fatigue Properties of the High Strength Aluminum Alloy 7475-T7351

Popis výsledku v původním jazyce

The hard complex inclusions Fe-Cu-C-O were crucial for disturbing the material integrity and production of local stress risers and suppressed the role of surface roughness or selection of cutting conditions in the analyzed ranks. Neither the surface topography nor the imposed specific cutting energies were the key factors affecting the fatigue performance of the machined aluminum alloy 7475-T7351. Fatigue fracture analysis showed that the material inclusions dispersed in the adherent machined surfaces trigger the fatigue crack initiations and propagations. The next research is focused on the analysis of the mechanism in direct SEM tensile test observations and elimination of the material inhomogeneities.

Název v anglickém jazyce

A Study of Progressive Milling Technology on Surface Topography and Fatigue Properties of the High Strength Aluminum Alloy 7475-T7351

Popis výsledku anglicky

The hard complex inclusions Fe-Cu-C-O were crucial for disturbing the material integrity and production of local stress risers and suppressed the role of surface roughness or selection of cutting conditions in the analyzed ranks. Neither the surface topography nor the imposed specific cutting energies were the key factors affecting the fatigue performance of the machined aluminum alloy 7475-T7351. Fatigue fracture analysis showed that the material inclusions dispersed in the adherent machined surfaces trigger the fatigue crack initiations and propagations. The next research is focused on the analysis of the mechanism in direct SEM tensile test observations and elimination of the material inhomogeneities.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20304 - Aerospace engineering

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2018

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

International Conference on New Trends in Fatigue and Fracture

ISBN

978-3-319-70364-0

ISSN

—

e-ISSN

—

Počet stran výsledku

11

Strana od-do

7-17

Název nakladatele

Springer

Místo vydání

New York

Místo konání akce

Cancun

Datum konání akce

25. 10. 2017

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—