Microstructural changes of amorphous Mo–B–C coatings upon thermal annealing

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389005%3A_____%2F19%3A00510346" target="_blank" >RIV/61389005:_____/19:00510346 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68081723:_____/19:00510346 RIV/00216224:14310/19:00107713

Výsledek na webu

<a href="https://www.sciencedirect.com/science/article/pii/S0257897219310436?via%3Dihub" target="_blank" >https://www.sciencedirect.com/science/article/pii/S0257897219310436?via%3Dihub</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.surfcoat.2019.125052" target="_blank" >10.1016/j.surfcoat.2019.125052</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Microstructural changes of amorphous Mo–B–C coatings upon thermal annealing

Popis výsledku v původním jazyce

Several amorphous Mo–B–C coatings with wide range of compositions were subjected to thermal annealing to a final temperature of 1000 °C in UHV conditions. The nature of the induced recrystallization depended mostly on the Mo content in the coating. A higher Mo content resulted in a nanocrystalline Mo2C phase, a lower Mo content in a nanocrystalline Mo2BC phase and Mo content in-between resulted only in a near-amorphous microstructure. In all cases, the hardness and effective elastic modulus increased significantly after annealing up to values of ∼29 GPa and 500 GPa, respectively. The cobalt diffusion from the WC-Co substrates affected the lower parts of coatings forming a MoCoB interface.

Název v anglickém jazyce

Microstructural changes of amorphous Mo–B–C coatings upon thermal annealing

Popis výsledku anglicky

Several amorphous Mo–B–C coatings with wide range of compositions were subjected to thermal annealing to a final temperature of 1000 °C in UHV conditions. The nature of the induced recrystallization depended mostly on the Mo content in the coating. A higher Mo content resulted in a nanocrystalline Mo2C phase, a lower Mo content in a nanocrystalline Mo2BC phase and Mo content in-between resulted only in a near-amorphous microstructure. In all cases, the hardness and effective elastic modulus increased significantly after annealing up to values of ∼29 GPa and 500 GPa, respectively. The cobalt diffusion from the WC-Co substrates affected the lower parts of coatings forming a MoCoB interface.

Druh

J_SC - Článek v periodiku v databázi SCOPUS

CEP obor

—

OECD FORD obor

10302 - Condensed matter physics (including formerly solid state physics, supercond.)

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2019

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Surface and Coatings Technology

ISSN

0257-8972

e-ISSN

—

Svazek periodika

379

Číslo periodika v rámci svazku

DEC

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

7

Strana od-do

125052

Kód UT WoS článku

000498752500008

EID výsledku v databázi Scopus

2-s2.0-85073072737